流动条件下炔氧基甲季胺盐的缓蚀性能研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (4): 234-239

研究报告

本期目录 | 过刊浏览

流动条件下炔氧基甲季胺盐的缓蚀性能研究

蒋秀

Inhibitor Properties of Quaternary Alkynoxymethyl Amine Under Flowing Conditions

全文: PDF(206 KB)

摘要: 利用交流阻抗（EIS）、线性极化、动电位极化和失重法，研究了炔氧甲基季胺盐对N80在常温CO2饱和的3%NaCl溶液中的电化学行为和缓蚀性能的影响。结果表明：空白溶液中N80的累计失重在4m/s以后急剧增大，即介质的临界流速为4-5m/s。动态下炔氧甲基胺盐存在与静态下相同的浓度极值现象，流速低于5m/s时缓蚀剂的极值浓度与静态时相同，都为150mg/L，而流速高于5m/s后极值浓度有所增加。

关键词 ：炔氧甲基季胺盐, 临界流速, 电化学测试, 浓度

Abstract：The effect of IMC-80-Q(quaternary alkynoxymethyl amine) on the electrochemical behavior and inhigitor properties of N80 steel in 3% NaCl saturated by CO2 at 25℃ 1℃ under flowing conditions had been studied by weight loss and electrochemical techniques including EIS and linear polarization by using rotating discelectrode. The results showed that the cumulative mass loss increased greatly in the blank solution when flow velocity was higher than 4m/s, and the critical flow velocity for the blank solution was about 4-5m/s. The extreme-value-phenomena of concentration existed for IMC-80-Q under both flowing and static condition. 150mg/L was the best inhibitor concentration when flow velocity was lower than 5m/s. In contrast, higher inhibitor concentration(300mg/L for 7m/s and 9m/s) was required if flow velocity was higher than 5m/s.

Key words： quaternary alkynoxymethyl amine critical flow velocity electrochemical technique extreme-value-pheno

收稿日期: 2003-03-15

ZTFLH:

TG174.42

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	蒋秀
44.8K

引用本文:

蒋秀 . 流动条件下炔氧基甲季胺盐的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2004, 24(4): 234-239 .

链接本文:

https://www.jcscp.org/CN/Y2004/V24/I4/234

[1]GuoXP ,FuCY .InteractionbetweeninhibitorandCO2 corrosionpro ductionfilm[A].Qingdao:InhibitorCommitteeofChineseCorrosionandProtection,2001,7-12(郭兴蓬,付朝阳.缓蚀剂和CO2腐蚀产物膜的相互作用[A].青岛:中国腐蚀与防护学会缓蚀剂专业委员会,2001,7-12)
[2]DoughertyJA ,StergmannDW .Theeffectsofflowoncorrosionin hibitorsperformance[J].Mater.Perform.,1996,35(4):47-53
[3]LiuXW ,PengFM ,ZhengJS ,etal.Studyofinhibitorforpipelineinoilfields[J].Mater.Prot.,2000,33(8):3-5(刘小武,彭芳明,郑家焱木等.输油管线缓蚀剂的研究[J].材料保护,2000,33(8):3-5)
[4]ChenY ,JepsonWP .EISmeasurementforcorrosionmonitoringundermultiphaseflowcondition[J].ElectrochemicalActa,1999,(44):4453-4464
[5]WangHB ,HongT ,JepsonWP ,etal.Characterizationofinhibitorandcorrosionproductfilmusingelectrochemicalimpedancespectroscopy(EIS)[J].Corrosion,2001,01023
[6]SmartJS .ThemeaningoftheAPI -RP-14-Eformulaforerosioncorrosioninoilandgasproduction[J].Corrosion,1991,468
[7]JiangX ,ZhengYG ,KeW ,etal.Studyoninhibitorpropertiesofquater naryalkynoxymethylamineandimidazolineforN80seamlesssteelin3%NaClsaturatedbyCO2[J].J.Chin.Soc.Corros.Prot.,2004,24(1):10-15(蒋秀,郑玉贵,柯伟等.炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3%NaCl溶液中的缓蚀性能研究[J].中国腐蚀与防护学报,2004,24(1):10-15)
[8]WangJ ,CaoCN .AnodicdesorptionofinhibitorsⅡ.Effectsofinhibitordesorptiononelectrodeimpedance[J].J.Chin.Soc.Corros.Prot.,1995,15(4):247-253(王佳,曹楚南.缓蚀剂阳极脱附现象的研究Ⅱ.缓蚀剂阳极脱附对电极阻抗的影响[J].中国腐蚀与防护学报,1995,15(4):247-253)
[9]YangF ,ZhengYG ,YaoZM ,KeW .Studyonerosion-corrosionbe haviorofCu-NialloyBFe30-1-1inflowingartificialseawater[J].J.Chin.Soc.Corros.Prot.,1999,19(4):207-213(杨帆,郑玉贵,姚治铭,柯伟.铜镍合金BFe30-1-1在流动人工海水中的腐蚀行为[J].中国腐蚀与防护学报,1999,19(4):207-213)
[10]CaoCN .CorrosionElectrochemistry[M].Beijing:ChemistryIndustryPress,1994:328-344(曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994:328-344)
[11]MalikH .InfluenceofC16quaternaryamineonsurfacefilmsandpolar izationresistanceofmildsteelincarbondioxide-saturated5%sodiumchloride[J].Corrosion,1995,51(4):321-328

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[3]	沈树阳, 王东胜, 孙士斌, 杨剔, 赵前进, 王鑫, 张亚飞, 常雪婷. 深冷处理对EH40极寒环境船用钢板的海水腐蚀性能影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 151-158.
[4]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[5]	戚鹏, 万逸, 曾艳, 郑来宝, 张盾. 海洋环境中硫酸盐还原菌的快速测定方法研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 387-394.
[6]	严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[7]	廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na₂CO₃+NaHCO₃溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[8]	崔明君,任思明,张广安,刘栓,赵海超,王立平,薛群基. 六方氮化硼掺杂水性环氧树脂耐腐蚀性能的研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 566-572.
[9]	汪江伟,张杰,陈守刚,段继周,侯保荣. 钙质层对Q235碳钢在含双眉藻f/2培养基中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(6): 535-542.
[10]	董洋洋, 黄峰, 程攀, 胡骞, 刘静. X65 MS耐酸管线钢在H₂S环境中腐蚀产物膜的演变[J]. 中国腐蚀与防护学报, 2015, 35(5): 386-392.
[11]	苏铁军, 罗运柏, 李克华, 李凡修, 邓仕英, 习伟. 苯并咪唑-N-曼尼希碱对盐酸中N80钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2015, 35(5): 415-422.
[12]	张丹丹,王振尧,赵春英,曹公望. Q345钢在模拟酸性海洋气溶胶环境下的大气腐蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(4): 326-332.
[13]	王青, 马雪梅, 石海燕, 原珊, 郭建峰, 梁栋, 胡志勇. 苯并咪唑衍生物在1 mol/L HCl溶液中对45^#碳钢缓蚀行为的研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 49-54.
[14]	邢云颖, 刘智勇, 杜翠薇, 李晓刚, 刘然克, 朱敏. H₂S浓度和pH值对X65海管钢焊接接头腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2014, 34(3): 231-236.
[15]	鞠玉琳, 李焰. 气相缓蚀剂的研究进展[J]. 中国腐蚀与防护学报, 2014, 34(1): 27-36.

Viewed

Full text

Abstract

Cited

Shared

Discussed