镉-钛镀层导致30CrMnSiNi2A钢后脆的研究
秦月文;熊家锦;吴再思;刘佑厚
北京航空材料研究所;北京航空材料研究所;北京航空材料研究所;北京航空材料研究所
A STUDY OF THE POST-PLATING EMBRITTLEMENT OF Cd-Ti COATED 30CrMnSiNi2A STEEL
Qin Yuewen Xiong Jiajin Wu Zaisi and Liu Youhou(Institute of Aeronatical Materials; Beijing; China)
全文: PDF(1869 KB)  
摘要: 本文采用棒材缺口试样研究了Cd-Ti镀层在3.5%NaCl介质中引起30CrMnSiNi2A钢后脆的现象。通过不同通气条件下恒电位极化破断试验,电化学渗氢试验、阴极极化曲线的测定、人工闭塞电池等的研究,以及对断口形貌特征的分析,讨论了Cd-Ti镀层后脆产生的原因。
Abstract:The post-plating embri ttlement of Cd-Ti coated high strength steel 30CrMnSiNi2A in 3.5% NaCl solution has been studied. Notched specimens are used for tests. The stress vs time to fracture curves under potentiostatic polarization, the potentiodynamic cathodic polarization curve and the electrochemical hydrogen permeability have been measured under different aerated conditions. The phenomenon of the auto-acidification in artificial occluded cell and the characteristic fractography of the notched specimens have been observed and analyzed. The reason for post-plating embrittlement of Cd-Ti coated high strength steel and the way to avoid such embrittlement have been suggested.
收稿日期: 1983-04-25     

引用本文:

秦月文;熊家锦;吴再思;刘佑厚. 镉-钛镀层导致30CrMnSiNi2A钢后脆的研究[J]. 中国腐蚀与防护学报, 1983, 3(2): 97-103.
. A STUDY OF THE POST-PLATING EMBRITTLEMENT OF Cd-Ti COATED 30CrMnSiNi2A STEEL. J Chin Soc Corr Pro, 1983, 3(2): 97-103.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y1983/V3/I2/97

[1] 秦月文、刘佑厚, 高强度钢无氰镀镉-钛的研究,航空材料,12(1980)
[2] 阎秀成,电镀与氢脆,国外航空, 4,52(1977)
[3] J. Rinker and R. Hochman, Corrosion,28. 6, 231(1972)
[4] D. Altura, Metal Finishing,72, 9, 45(1974)
[5] M, A. V. Devanathan and Z. Stachurski, Proceedings of the Royal Society Series A, 270, 1340, 90 ( 1962 )
[6] 左景伊等,腐蚀裂缝内化学和电化学状态之探索,中国腐蚀与防护学会电化学分会第一届学术年会报告, (1981)
[7] P. A. Parrish , C. M. Chen and E. D. Verink . JR , Stress Corrosion-New Approaches, ASTM STP 610, 189(1976)
[8] 左景伊,应力腐蚀破裂,中国腐蚀与防护学会,腐蚀理论学习班教材, (1980)
[9] C. F. Barth and A. R. Troiano, Corrosion, 28, 7, 259(1972)
[10] B. E. Wilde, Corrosion, 27, S. 326(1971)
No related articles found!