镀锌层破损输电杆塔用镀锌钢在干湿交替作用下的腐蚀行为 |
原徐杰1,2, 张俊喜1, 张世明1, 谈天1 |
1. 上海电力学院 上海高校电厂腐蚀防护与应用电化学重点实验室 上海 200090; 2. 上海中挪海事技术有限公司 上海 201417 |
|
Corrosion Behavior of Galvanized Steel for Power Transmission Tower with Breakage of Zinc #br#Coating in Polluted Environment |
YUAN Xujie1,2, ZHANG Junxi1, ZHANG Shiming1, TAN Tian1 |
1. Key Laboratory of Shanghai Colleges and Universities for Electric Power Corrosion Control and Applied Electrochemistry, Shanghai University of Electric Power, Shanghai 200090, China; 2. Shanghai CCS-DNV Technology Institute, Shanghai 201417, China |
引用本文:
原徐杰, 张俊喜, 张世明, 谈天. 镀锌层破损输电杆塔用镀锌钢在干湿交替作用下的腐蚀行为[J]. 中国腐蚀与防护学报, 2013, 33(5): 395-399.
YUAN Xujie,
ZHANG Junxi,
ZHANG Shiming,
TAN Tian.
Corrosion Behavior of Galvanized Steel for Power Transmission Tower with Breakage of Zinc #br#Coating in Polluted Environment. Journal of Chinese Society for Corrosion and protection, 2013, 33(5): 395-399.
链接本文:
https://www.jcscp.org/CN/
或
https://www.jcscp.org/CN/Y2013/V33/I5/395
|
[1] Me Z L, Cheng Z Y. Corrosion and prevention of zinc deposit of transmission towers [J]. Electric Power Constr., 2004, 25(1): 22-23 (默增禄, 程志云. 输电线路杆塔的腐蚀与防治对策 [J]. 电力建设, 2004, 25(1): 22-23 [2] Chen Y, Qiang C M, Wang G G, et al. Corrosion and protection of transmission towers [J]. Electric Power Constr., 2010, 31(8): 55-58 (陈云, 强春媚, 王国刚等. 输电杆塔的腐蚀与防护 [J]. 电力建设, 2010, 31(8): 55-58) [3] Zhang X G, Vahriote E M. Galvanic protection of steel and galvanic corrosion of zinc under thin layer electrolytes [J]. Corros. Sci., 1993, 34(12): 1957-1972 [4] Shevchuk P R, Galapats B P, Lakh Y V. A study of corrosion damage of metal anode coatings in electrolytes [J]. J. Math. Sci., 1996, 79(6): 1426-1430 [5] Zhang X G, Li C W, Qi H B. Corrosion behavior and mechanism of the automotive hot-dip galvanized steel with alkaline mud adhesion [J]. Int. J. Miner. Metall. Mater., 2009, 16(4): 414-421 [6] Yadav A P, Katayama H, Noda K, et al. Surface potential distribution over a zinc/steel galvanic couple corroding under thin layer of electrolyte [J]. Electrochim. Acta, 2007, 52(9): 3121-3125 [7] Zhang H, Du C W, Li X G,et al. The influences of the broken area of zinc coating on the electrochemical corrosion behavior of auto galvanized steel sheet in mud [A]. National Science Seminar on the Hydrogen-brittlenes and Stress and the Engineering Application [C]. Jiangyou: 2007 (张红, 杜翠薇, 李晓刚等. 泥浆中镀锌层破损汽车钢板腐蚀的电化学腐蚀行为研究 [A]. 全国氢脆与应力腐蚀及工程应用学术研讨会论文集 [C]. 江油: 2007) [8] Zhang H, Du C W, Qi H B, et al. Corrosion properties of galvanized auto steel sheet with breakages of zinc coating in NaCl containing solution and mud [J]. Corros. Sci. Prot. Technol., 2009, 21(3): 333-336 (张红, 杜翠薇, 齐慧滨等. 镀锌层破损汽车钢板在含NaCl溶液和泥浆中的腐蚀行为与EIS研究 [J]. 腐蚀科学与防护技术, 2009, 21(3): 333-336) [9] Zhang H, Du C W, Li X G, et al. Corrosion properties of auto galvanized steel sheet with various broken areas of the zinc coating [J]. J. Chin. Soc. Corros. Prot., 2009, 29(3): 172-176 (张红, 杜翠薇, 李晓刚等. 镀锌层破损汽车钢板的腐蚀行为研究 [J]. 中国腐蚀与防护学报, 2009, 29(3): 172-176) [10] Zhang D L, Wang W, Li Y. Wire beam electrode technique for investigating galvanic corrosion behavior of hot dip galvanized steel-scratch defect [J]. Chin. J. Mater. Res., 2009, 23(4): 343-346 (张大磊, 王伟, 李焰. 热镀锌钢材的电偶腐蚀行为-划痕型缺陷 [J]. 材料研究学报, 2009, 23(4): 343-346) [11] Zhang D L, Wang W, Jin Y H, et al. Wire beam electrode technique for investigating galvanic corrosion behavior of galvanized steel-spot defect [J]. Chin. J. Nonferrous Met., 2011, 21(9): 2168-2174 (张大磊, 王伟, 金有海等. 丝束电极研究镀锌层存在点缺陷的锌/钢电偶腐蚀行为 [J]. 中国有色金属学报, 2011, 21(9): 2168-2174) [12] ASTM D 5032-1997. Standard Practice for Maintaining Constant Relative Humidity by Means of Aqueous Glycerin Solutions [S]. West Conshohlcken: ASTM International, 2003 [13] Qu Q, Yan C W, Zhang L, et al. Synergism of NaCl and SO2 in initial atmospheric corrosion of Zn [J]. Chin. J. Nonferrous Met., 2002, 12(6): 1272-1276 (屈庆, 严川伟, 张蕾等. Zn初期大气腐蚀中NaCl和SO2的协同效应 [J]. 中国有色金属学报, 2002, 12(6): 1272-1276) [14] Hamlaoui Y, Pedraza F, Tifouti L. Corrosion monitoring of galvanized coatings through electrochemical impedance spectroscopy [J]. Corros. Sci., 2008, 50(6): 1558-1566 [15] Cao C N. Corrosion Electrochemistry [M]. Beijing: Chemistry Industry Press, 2005 (曹楚南. 腐蚀电化学 [M]. 北京: 化学工业出版社, 2005 ) |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|