中国腐蚀与防护学报  2013, Vol. 33 Issue (4): 306-310    
  研究报告 本期目录 | 过刊浏览 |
Cu在北京土壤环境中的腐蚀行为
朱 敏 杜翠薇 李晓刚 刘智勇 李月强 黄 亮
北京科技大学材料科学与工程学院 北京 100083
Corrosion Behavior of Pure Copper in Beijing Soil Environment
ZHU Min, DU Cuiwei, LI Xiaogang, LIU Zhiyong, LI Yueqiang, HUANG Liang
School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
全文: PDF(2723 KB)  
摘要: 通过现场实验(1,2和2.5 a)和电化学阻抗谱(EIS)测试,并结合腐蚀形貌宏观观察, SEM, XRD及失重法对纯Cu在北京土壤环境中的腐蚀行为及机理进行了研究。结果表明:现场埋样1,2和2.5 a的纯Cu的腐蚀特征均为非均匀的全面腐蚀,腐蚀程度较轻微。随埋样时间的延长,纯Cu的腐蚀速率近乎呈线性关系减小,岛屿状腐蚀产物中的空隙等缺陷减少,其致密性有所改善。腐蚀产物均主要由Cu2(CO3)(OH)2, CuO3H2O和CuCl组成。
关键词 纯Cu北京土壤EIS腐蚀行为    
Abstract:The corrosion behavior of pure copper in Beijing soil environment was investigated by burying test in nature field for 1, 2 and 2.5 a, electrochemical impedance spectroscopy(EIS), macro-morphology, SEM, XRD and weight-loss method. The results showed that nonuniform general corrosion occurred mainly on the pure copper in Beijing soil, with the slight corrosion. The corrosion rate of pure copper nearly decreased linearly with the increase of burying time, while the defects in island-like corrosion product reduced, and the compactness of the corrosion product improved. The corrosion products mainly consisted of Cu2(CO3)(OH)2, CuO3H2O and CuCl.
Key wordspure copper    Beijing soil    EIS    corrosion behavior
    
ZTFLH:  TG172.4  

引用本文:

朱敏, 杜翠薇, 李晓刚, 刘智勇, 李月强, 黄亮. Cu在北京土壤环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2013, 33(4): 306-310.
ZHU Min, DU Cuiwei, LI Xiaogang, LIU Zhiyong, LI Yueqiang, HUANG Liang. Corrosion Behavior of Pure Copper in Beijing Soil Environment. Journal of Chinese Society for Corrosion and protection, 2013, 33(4): 306-310.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2013/V33/I4/306

[1] Yu H, Dong S Y, Xu H B, et al. Study on the electrochemical impedance spectroscopy(EIS) of Al-bronze at different anodic potentials[J]. Electrochemistry, 2004, 10(1): 35-40
(于辉, 董飒英, 徐海波等.不同阳极电位下铝青铜的电化学阻抗谱研究 [J]. 电化学, 2004, 10(1): 35-40)
[2] Liu Q, Wang Q J, Du Z Z. The research of copper corrosion in natural environment [J]. New Technol. New Process, 2008, (8): 81-82
(刘琼, 王庆娟, 杜忠泽. 铜在自然环境中的腐蚀研究 [J]. 新技术新工艺, 2008, (8): 81-82)
[3] Meng X L. A study of corrosion of mild steel in soil [J]. J. Chin. Soc. Corros. Prot., 1997, 17(4): 291-294
(孟厦兰. 苏打盐土中低碳钢的自然腐蚀规律 [J]. 中国腐蚀与防护学报, 1997, 17(4): 291-294)
[4] Li M C, Lin H C, Cao C N. Study on soil corrosion of carbon steel by electrochemical impedance spectroscopy(EIS) [J]. J. Chin. Soc. Corros. Prot., 2000, 20(2): 111-117
(李谋成, 林海潮, 曹楚南. 碳钢在土壤中腐蚀的电化学阻抗谱特征 [J]. 中国腐蚀与防护学报, 2000, 20(2): 111-117)
[5] Lorenz W J, Mansfeld F. Determination of corrosion rates by electrochemical DC and AC methods [J]. Corros. Sci., 1981, 21(9): 647-672
[6] Murray J N, Moran P J. Influence of moisture on corrosion of pipeline steel in soil using in-situ impedance spectroscopy [J]. Corrosion, 1989, 45(1): 34-42
[7] GB/T 16545-1996 Removal of corrosion products from corrosion test specimens of metals and alloys [S]. Beijing: National Quality Supervision, 1996
(GB/T16545-1996金属和合金的腐蚀试样上腐蚀产物的清除 [S]. 北京: 国家技术监督局, 1996)
[8] Li X G, Du C W, Dong C F, et al. Corrosion Behavior and Test of X70 Pipeline Steel [M]. Beijing: Science Publishing, 2006
(李晓刚, 杜翠薇, 董超芳等. X70钢的腐蚀行为与试验研究 [M]. 北京: 科学出版社, 2006)
[9] Xia Y S, Wang Y H, Lu Z H, et al. Short-term corrosion behavior of Cu, Pb and Al in Kuerle desert soil [J]. Equip. Environ. Eng., 2008, 5(5): 21-24
(夏永生, 王永红, 鹿中晖等. 铜铅铝在库尔勒荒漠土中的短期腐蚀行为 [J]. 装备环境工程, 2008, 5(5): 21-24)
[1] 李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[2] 张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[3] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4] 王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[5] 胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[6] 张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[7] 苏小红,胡会娥,孔小东. W颗粒/Zr41.2Ti13.8Cu12.5Ni10Be22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[8] 王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[9] 郭铁明,张延文,秦俊山,宋志涛,董建军,杨新龙,南雪丽. 桥梁钢Q345q在3种模拟大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 319-330.
[10] 黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[11] 曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II:涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[12] 张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[13] 蔡光义,王浩伟,赵苇杭,董泽华. 添加纳米CeO2对聚氨酯涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 411-420.
[14] 张子阳,王善林,章恒瑜,柯黎明. AZ31镁合金搅拌摩擦焊接头腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(2): 117-125.
[15] 刘栓,周开河,方云辉,徐孝忠,江炯,郭小平,郑文茹,蒲吉斌,王立平. 环境因素对纯Zn在饱和Zn(OH)2溶液中腐蚀行为的影响I—Cl-浓度和pH值[J]. 中国腐蚀与防护学报, 2016, 36(6): 522-528.