2-氨基吡啶缩水杨醛席夫碱对Q235钢在盐酸介质中的缓蚀性能

罗亮

南京工业大学理学院南京 210009

Inhibition of 2-((Pyridin-2-Ylimino) Methyl) Phenol for Q235 Steel in 1 mol/L HCl Solution

LUO Liang

College of Science, Nanjing University of Technology, Nanjing 21009, China

全文: PDF(673 KB)

摘要: 合成了一种吡啶衍生物：2-氨基吡啶缩水杨醛席夫碱(PMP)，并通过静态失重、动电位极化曲线和电化学阻抗谱等方法，研究了其对Q235钢在1 mol/L HCl溶液中的缓蚀性能。结果表明，在(30±1) ℃下1 mol/L HCl溶液中，当PMP浓度达到15.0 mmol/L时，缓蚀效率为87.9%，是以阴极型为主的混合型缓蚀剂。PMP在Q235钢表面吸附符合Langmuir吸附等温式，吸附过程包括物理吸附和化学吸附。

关键词 ：缓蚀剂, 吡啶, 吸附, 电化学测试

Abstract：A new pyridine derivative, 2-((pyridine-2-ylimino)methyl)phenol (PMP) was synthesized and its inhibition effect in 1 mol/L HCl for Q235 steel was studied by means of mass loss measurement, potentiodynamic polarization and electrochemical impedance spectroscopy. Generally, the results indicate that PMP has excellent inhibiting effect. The inhibition efficiency increases with the increase of inhibitor concentration in 1mol/L HCl and the inhibition efficiency is up to 87.9% at the concentration of 15.0 mmol/L. The electrochemical measurements show that PMP acts as a mixed type inhibitor with cathodic inhibition as dominative action. The adsorption of PMP on the Q235 steel surface obeys the Langmuir adsorption law and contains both physisorption and chemisorption.

Key words： inhibitor pyridine adsorption electrochemical measurement

ZTFLH:

TG174.42

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	罗亮
44.8K

引用本文:

罗亮. 2-氨基吡啶缩水杨醛席夫碱对Q235钢在盐酸介质中的缓蚀性能[J]. 中国腐蚀与防护学报, 2013, 33(3): 221-225.
LUO Liang. Inhibition of 2-((Pyridin-2-Ylimino) Methyl) Phenol for Q235 Steel in 1 mol/L HCl Solution. Journal of Chinese Society for Corrosion and protection, 2013, 33(3): 221-225.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2013/V33/I3/221

[1] Zhang T S. Corrosion Inhibitors [M]. Beijing: Chemical Industry Press, 2001
(张天胜. 缓蚀剂 [M]. 北京: 化学工业出版社, 2001 )
[2] Xie B, Lai C, Zou L K, et al. Inhibition of N, N-diethylammonium O, O’-dicyclohexyldithiophosphate for Q235 steel in sulfuric solution [J]. J. Chin. Soc. Corros. Prot., 2011, 31(3): 225-230
(谢斌, 赖川, 邹立科等. O,O’-二(环己基)二硫代磷酸-N,N-二乙铵对Q235钢在硫酸溶液中的缓蚀性能研究 [J]. 中国腐蚀与防护学报, 2011, 31(3): 225-230)
[3] Hosseni M, Mertens S F L, Ghorbani M, et al. Asymmetrical Schiff bases as inhibitors of mild steel corrosion in sulphuric acid media [J]. Mater. Chem. Phys., 2003, 78: 800-808
[4] Qauraishi M A, Ansari F A, Jamal D. Thiourea derivatives as corrosion inhibitors for mild steel in formic acid [J]. Mater. Chem. Phys., 2002, 77: 687-690
[5] Zhang S T, Tao Z H, Li W H, et al. A corrosion inhibition of mild steel by novel triazole compound in 1 mol/L HCl solution [J]. J. Chin. Soc. Corros. Prot., 2009, 29(6): 487-492
(张胜涛, 陶志华, 李伟华等. 新型三氮唑化合物在1 mol/L HCl中对Q235钢的缓蚀性能 [J]. 中国腐蚀与防护学报, 2009, 29(6): 487-492)
[6] Xie Q F, Li X L. Synthesis and characterization of the transition-metallic complex with a phenanthroline and a schiff base ligand derived from α-amino pyridine and salicylaldehyde [J]. Chem. Eng. Equip., 2008, 9(3): 14-18
(解庆范, 李晓玲. α-氨基吡啶缩水杨醛希夫碱-邻菲罗啉过渡金属配合物的合成及表征 [J]. 化学工程与装备, 2008, 9(3): 14-18)
[7] Solmaz R, Kardas G, Yazici B, et al. Adsorption and corrosion inhibitive properties of 2-amino-5-mercapto-l, 3, 4-thiadiazole on mild steel in hydrochloric acid media [J]. Colloids Surf., 2008, 312(1)A: 7-17
[8] Tang Y M, Yang X Y, Yang W Z, et al. A preliminary investigation of corrosion inhibition of mild steel in 0.5 M H₂SO₄ by 2-amino-5-(n-pyridyl)-1,3,4-thiadiazole: Polarization, EIS and molecular dynamics simulations [J]. Corros. Sci., 2010, 52: 1801-1808

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[4]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[5]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[6]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[7]	李向红, 邓书端, 徐昕. 木薯淀粉三元接枝共聚物对钢在H₂SO₄溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 105-114.
[8]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[9]	沈树阳, 王东胜, 孙士斌, 杨剔, 赵前进, 王鑫, 张亚飞, 常雪婷. 深冷处理对EH40极寒环境船用钢板的海水腐蚀性能影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 151-158.
[10]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[11]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[12]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[13]	严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[14]	刘建国,高歌,徐亚洲,李自力,季菀然. 咪唑啉类衍生物缓蚀性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[15]	李亚琼,马景灵,王广欣,朱宇杰,宋永发,张景丽. NaPO₃与SDBS缓蚀剂对AZ31镁合金空气电池在NaCl电解液中放电性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.

Viewed

Full text

Abstract

Cited

Shared

Discussed