| 深海钢铁材料的阴极保护技术研究及发展 |
| 李成杰,杜敏 |
| 中国海洋大学化学化工学院 海洋化学理论与工程技术教育部重点实验室 青岛 266100 |
|
| Research and Development of Cathodic Protection for Steels in Deep Seawater |
| LI Chengjie, DU Min |
| The Key Laboratory of Marine Chemistry Theory and Technology, Ministry of Education, College of Chemistry and Chemical Engineering ,Ocean University of China, Qingdao 266100, China |
[1] Li R P, Xie Y H, Shu Z. A review on the technical development of deep water offshore platform [J]. China Offshore Platform, 2003, 18(3): 1-5(李润培, 谢永和, 舒志. 深海平台技术的研究现状与发展趋势[J]. 中国海洋平台, 2003, 18(3): 1-5)
[2] NACE Standard RP0176-2003, Corrosion control of steel fixed offshore structures associated with petroleum production [S].
[3] Recommended Reactive DNV-RP-B401, Cathodic protection design [S].
[4] Fischer K P. Deep water: considerations of the cathodic protection design basis [A]. Offshore Technology Conference [C]. Houston: 1999
[5] Hou J, Guo W M, Deng C L. Influences of deep sea environmental factors on corrosion behavior of carbon steel [J]. Equip. Environ. Eng., 2008, 5(6): 6-9(侯健, 郭为民, 邓春龙. 深海环境因素对碳钢腐蚀行为的影响 [J]. 装备环境工程, 2008, 5(6): 6-9)
[6] Cao Z Y. Study for calcareous deposits under initial cathodic protection in simulated deep ocean environment [D]. Qingdao: Ocean University of China, 2010(曹振宇. 模拟深海环境阴极保护初期钙镁沉积层的研究 [D]. 青岛: 中国海洋大学, 2010)
[7] Wen G M, Zheng F Y. Calcareous deposits formation and application of cathodic protection in seawater [J]. Corros. Prot., 1995, 16(1): 14-19(温国谋, 郑辅养. 海水中阴极保护时钙质沉积层的形成及其应用 [J]. 腐蚀与防护, 1995, 16(1): 50-53)
[8] Goolsby A D, Smith J D. Auger tension leg platform cathodic protection system [J]. Mater. Perform., 1996, 35(4): 12-17
[9] Lin S, Dexter S C. Effects of temperature and magnesium ions on calcareous deposition [J]. Corros. Sci., 1988, 44(9): 615-622
[10] Mantel K E, Hartt W H, Chen T. Substrate, surface finish, and flow rate influences on calcareous deposit structure [J]. Corrosion, 1992, 48(6): 489-500
[11] Barchiche C, Deslouis C, Festy D, et al. Characterization of calcareous deposits in artificial seawater by impedance techniques: 3-Deposit of CaCO3 in the presence of Mg (II) [J]. Electrochim. Acta, 2003, 48: 1645-1654
[12] Deslouis C, Festy D, Gil O, et al. Characterization of calcareous deposits in artificial sea water by impedance techniques—2. Deposit of Mg(OH)2 without CaCO3 [J]. Electrochim. Acta, 2000, 45(12-13): 1837-1845
[13] Brown B F, Foreson B W, Lennos T J, et al. Marine corrosion studies: stress corrosion cracking, deep ocean technology, cathodic protection, corrosion fatigue [A]. Third interim report of progress [C]. US: US Naval Research Laboratory, 1965
[14] Fischer K P, Finnegan J E. Cathodic polarization behavior of steel in seawater and the protective properties of the calcareous deposits [A]. Corrosion/89 [C]. Houston: NACE, 1989
[15] MacKay W B. Deep water testing of sacrificial anodes part 2 [A].Corrosion/75 [C]. Houston, 1975
[16] England H R, Heidersbach R H. The effects of water depth on cathodic protection [A]. Corrosion/82 [C]. Houston: NACE, 1982
[17] England H R, Heidersbach R H. Deep water effects on cathodic protection [A]. 14th Annual Offshore Technology Conference [C]. Houston: NACE 1982
[18] Tawns A, Stena C, Limited O, et al. Cathodic protection at a simulated depth of 2500 m [A]. Corrosion2000 [C]. Orlando, Fl: NACE, 2000
[19] Li C J, Du M, Li Y, et al. The influences of protection potentials on the formation of calcareous deposits in dynamic seawater [J]. Periodical Ocean Univ. Chin., 2011, 41(7/8): 149-153(李成杰, 杜敏, 李妍等. 动态海水中保护电位对钙质沉积层形成的影响 [J]. 中国海洋大学学报, 2011, 41(7/8): 149-153)
[20] Fischer K P, Sydberger T, Lye R. Field testing of deep water cathodic protection on the Norwegian Continental Shelf [J]. Mater. Perform., 1988, 27(1): 49-56
[21] Finegan J E, Fischer K P. Calcareous deposits: calcium and magnesium ion concentrations [A]. Corrosion/89 [C]. Houston: NACE, 1989
[22] Chen S, Hartt W H. Deepwater cathodic protection. Part 1: laboratory simulation experiments [J]. Corrosion, 2002, 58(1): 38-48
[23] Goolsby A D, Wolfoson S L. Extended cathodic protection monitoring of one of the world's deepest fixed offshore platforms-Bullwinkle [A]. Corrosion/98 [C]. Houston: NACE, 1998
[24] Fischer K P, Espelid B, Veritas D N. A review of cp current demand and anode performance for deepwater [A]. Corrosion 2001 [C]. Houston: NACE, 2001
[25] Chen S, Hartt W H, Wolfson S. Deep water cathodic protection. Part 2: field deployment results [J]. Corrosion, 2003, 59(8): 721-732
[26] Fischer K P, Sydberger T. In-situ testing of cathodic protection on the Northern Norwegian Continental Shelf [A]. Corrosin/84 [C]. Houston: NACE, 1984
[27] Fischer K P. Field testing of CP current requirements at depths down to 1300 m on the Norwegian Continental Shelf from 63 to 67°N [A]. Corrosion/99 [C]. Houston: NACE, 1999
[28] Fischer K P, Thomason W H, Eliassen S. CP in deep water: The importance of calcareous deposits and the environmental conditions [A]. Corrosion/96 [C]. Houston: NACE, 1996
[29] Zuo J Y. Stress Corrosion Cracking [M]. Xi'an: Xi'an Jiaotong Universtiy Press,1985(左景伊. 应力腐蚀破裂 [M]. 西安: 西安交通大学出版社, 1985)
[30] ISO.155892-2-2002, Petroleum and natural gas industries- Cathodic protection of pipeline transportation systems. Part 2: Offshore pipelines [S].
[31] EN.12954-2001, Cathodic protection of buried or immersed metallic structures- General principles and application for pipelines [S].
[32] NACE. SP0169- 2007, Standard practice- control of external corrosion on underground submerged metellic piping systems[S].
[33] Zhang T, Sun X L, Chen J S, et al. Role of hydrogen in stress corrosion cracking of high strength pipeline steel [J]. Pipeline Technique Equip., 2004, (2): 33-35(张涛, 孙欣岭, 陈居术等. 氢在高强度管道钢应力腐蚀中的作用 [J]. 管道技术与设备, 2004, (2): 33-35)
[34] Hansung K, Popov B N, Chen K S. Comparison of corrosion-resistance and hydrogen permeation properties of Zn-Ni, Zn-Ni-Cd and Cd coatings on low-carbon steel [J]. Corros. Sci., 2003, 45(47): 1505-1521
[35] Shu D L. Mechanical Properties of Engineering Materials [M]. Beijing: Mechanical Industry Press, 2003(束德林. 工程材料力学性能 [M]. 北京: 机械工业出版社, 2003)
[36] Zhang L. Study on the cathodic protection process and susceptibility of hydrogen embrittlement of X70 steel in simulated deep ocean environment [D]. Qingdao: Ocean University of China, 2011(张林. 模拟深海环境X70钢阴极保护过程及其氢脆敏感性研究 [D]. 青岛: 中国海洋大学, 2011)
[37] Festy D. Cathodic protection of steel in deep sea: Hydrogen embrittlement risk and cathodic protection criteria [A]. Corrosion/2001 [C]. Houston: NACE, 2001
[38] Fairhurst D. Offshore cathodic protection: what we have learnt [J]. J. Corros. Sci. Eng., 2003, 4(6): 1-17
[39] Britton J N. External corrosion control and corrosion inspection of deepwater pipelines [A]. The 2nd International Deepwater Pipeline Technology Conference [C]. New Orleans: 1999
[40] Britton J N. Cathodic protection design in deep water, be safe not sorry [A]. Corrosion/99 [C]. San Antonio: NACE, 1999
[41] Liu X J. Anticorrosion coating technology and its progress in ocean environment[J]. Modern Paint Finish., 2010, 13(4): 20-22(刘晓建. 海洋环境中的防腐蚀涂层技术及发展 [J]. 现代涂料与涂装, 2010, 13(4): 20-22)
[42] Wolfson S L. Corrosion control of subsea piping systems using thermal sprayed aluminum coatings [J]. Mater. Perform., 1996, 35(7): 32-36
[43] Du Y X, Zhang G Z, Li J. Numerical calculation of cathodic protection potential distribution [J]. J. Chin. Soc. Corros. Prot., 2008, 28(1): 53-58(杜艳霞, 张国忠, 李健. 阴极保护电位分布的数值计算 [J]. 中国腐蚀与防护学报, 2008, 28(1): 53-58)
[44] Wang A P, Du M, Lu C S, et al. Finite element method for an offshore platform with complex nodes with a cathodic protection system [J]. Period. Ocean Univ. Chin., 2007, 37(1):129-134(王爱萍, 杜敏, 陆长山等. 海洋平台复杂节点阴极保护电位分布的有限元法计算 [J]. 中国海洋大学学报, 2007, 37(1): 129-134)
[45] Wang X T， Hou B R，Li Y. Boundary element method for the cathodic protection in sea mud [J]. Marine Sci., 2006, 30(12): 2-4(王秀通, 侯保荣, 李焰. 海泥环境中阴极保护的边界元计算 [J]. 海洋科学, 2006, 30(12): 2-4)
[46] Santiago J, Telles J C F. A solution technique for cathodic protection with dynamic boundary conditions by the boundary element method [J]. Adv. Eng. Software, 1999, 30: 663-671
[47] Montoya R, Galván J C, Genesca J. Using the right side of Poisson's equation to save on numerical calculations in FEM simulation of electrochemical systems [J]. Corros. Sci., 2011, 53(5): 1806-1812
[48] Chen G Z, Wang H R. Cathodic protection and anti-corrosion technology for marine structure [J]. Corros. Prot., 2008, 29(z1): 14-19（陈光章, 王洪仁. 海洋结构中的阴极保护防腐蚀技术 [J]. 腐蚀与防护, 2008, 29(z1): 14-19）
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|