天然气管线钢CO<sub>2</sub>腐蚀研究进展

中国腐蚀与防护学报

2013, Vol. 33

Issue (1): 1-9

综述

本期目录 | 过刊浏览

天然气管线钢CO₂腐蚀研究进展

刘玉¹, 李焰²

1. 中国石油大学(华东)化学工程学院青岛 266580;
2. 中国石油大学(华东)机电工程学院青岛 266580

Research Progress of CO₂ Corrosion of Internal Gas Pipeline Steel

LIU Yu¹, LI Yan²

1. College of Chemical Engineering, China University of Petroleum (East China), Qingdao 266580, China;
2. College of Mechanical and Electrical Engineering, China University of Petroleum (East China), Qingdao 266580, China

全文: PDF(8998 KB)

摘要:

天然气管线面临日益严重的CO₂腐蚀问题。针对管线内特定的腐蚀环境，总结了当前CO₂腐蚀在反应机理、影响因素以及腐蚀控制方面的研究进展，最后展望CO₂腐蚀研究今后的发展方向。

关键词 ：管线钢, CO₂腐蚀, 局部腐蚀

Abstract：

Gas pipelines are facing increasingly serious CO₂ corrosion problem. This paper introduced the specific corrosive environment within the gas pipeline, then summarized up the CO₂ corrosion research progress in reaction mechanism, influencing factors and current corrosion control measures. At last, the research direction of CO₂ corrosion of gas pipeline was proposed.

Key words： pipeline steel CO₂ corrosion localized corrosion

ZTFLH:

TE988

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘玉
	李焰
44.8K

引用本文:

刘玉,李焰. 天然气管线钢CO₂腐蚀研究进展[J]. 中国腐蚀与防护学报, 2013, 33(1): 1-9.
LIU Yu, LI Yan. Research Progress of CO₂ Corrosion of Internal Gas Pipeline Steel. Journal of Chinese Society for Corrosion and protection, 2013, 33(1): 1-9.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2013/V33/I1/1

[1] Luo P，Zhang Y L，Cai P P，et al．Analysis and countermeasures of natural gas transmission pipeline internal corrosion accidents [J]. Oil Gas，2010，6：16-21
(罗鹏，张一玲，蔡陪陪等. 长输天然气管道内腐蚀事故调查分析与对策 [J]. 石油与天然气，2010，6：16-21)
[2] Zhang Z H，Guo J B．Law of CO²corrosion of oil country tubular goods and the study of its progress at home and abroad [J]. Baosteel Technol.，2000，4：54-58
(张忠铧，郭金宝. CO²对油气管材的腐蚀规律及国内外研究进展 [J]. 宝钢技术，2000，4：54-58)
[3] Ikeda A，Veda M，Mukai S. CO²behavior of carbon and Cr steels [J]. Corrosion， 1984， 40(3)：289-301
[4] De Waard C，Milliams D E. Carbonic acid corrosion of steel [J]. Corrosion，1975，31(5)：177-181
[5] Ogundele G I，White W E. Some observation on corrosion of carbon steel in aqueous environments containing carbon dioxide [J]. Corrosion，1986，42(2)：68-74
[6] Gray L G S，Anderson B G，Danysh M J，et al．Mechanism of carbon steel corrosion in brines containing dissolved carbon dioxide at pH 4 [A]. Corrosion/89 [C]. Houston：NACE，1989
[7] Ne?i? S，Thevenot N，Crolet J L. Electrochemical properties of iron dissolution in CO² solutions-basics revisited [A]. Corrosion/96 [C]. Houston：NACE，1996
[8] Wang S，George K，Ne?i? S. High pressure CO² corrosion electrochemistry and the effect of acetic acid [A]. Corrosion/04 [C]. Houston： NACE，2004
[9] Garsany Y，Pletcher D，Hedges B. The role of acetate in CO² corrosion of carbon steel：has the chemistry been forgotten? [A]. Corrosion/02 [C]. Houston：NACE，2002
[10] Ezuber H M. Influence of temperature and thiosulfate on the corrosion behavior of steel in chloride solutions saturated in CO² [J]. Mater. Des.，2009，30：3420-3427
[11] Chokshi K，Sun W，Ne?i? S. Iron carbonate film growth and the effect of inhibition in CO² corrosion of mild steel [A]. Corrosion/05 [C]. Houston：NACE，2005
[12] Ne?i? S，Wang S，Cai J，et al. Integrated CO² corrosion-multiphase flow model [A]. Corrosion/04 [C]. Houston：NACE，2004
[13] Villarreal J，Laverde D，Fuentes C. Carbon-steel corrosion in multiphase slug flow and CO² [J]. Corros. Sci.，2006，48：2363-2379
[14] Pailassx R，Dieumeg A M，Estavo Y M. Corrosion control in the gathering system at lack sour gas field [A]. Corrosion/81 [C]. Houston：NACE，1981
[15] Amri J，Gulbrandsena E，Nogueira R P. The effect of acetic acid on the pit propagation in CO² corrosion of carbon steel [J]. Electrochem. Commun.，2008，10：200-203
[16] Crolet J L，TheveNot N，Dugstad A. Role of free acetic acid on the CO² corrosion of steels [A]. Corrosion/99 [C]. Houston：NACE，1999
[17] Sercombe M，Bailey S，De M R，et al. An investigation of the influence of acetic acid on carbon dioxide corrosion [A]. Corrosion and prevention conference proceedings [C]. Australia：Australian Corrosion Association，2004
[18] Crolet J L，Bonis M. Why so low free acetic acid thresholds in sweet corrosion at low p^co2? [A]. Corrosion/05 [C]. Houston：NACE，2005
[19] Nafday O A，Ne?i? N S. Iron carbonate film formation and CO² corrosion in the presence of acetic acid [A]. Corrosion/05 [C]. Houston：NACE，2005
[20] Zhang Y C，Pang X L，Qu S P，et al. The relationship between fracture toughness of CO² corrosion scale and corrosion rate of X65 pipeline steel under supercritical CO² condition [J]. Int. J. Greenhouse Gas Contr.，2011，5：1643-1650
[21] Pailassx R，Dieumeg A M，Estavo Y M. Corrosion control in the gathering system at lack sour gas field [A]. Corrosion/81 [C]. Houston：NACE，1981
[22] Gordon P，Bierwagen. Reflections on corrosion control by organic coatings [J]. Prog. Org. Coat.，1996，28：43-48
[23] Long F L，Zheng W J，Chen C F, et al. Influence of temperature，CO² partial pressure，flow rate and pH value on uniform corrosion rate of X65 pipeline steel [J]. Corros. Prot.，2005，26(7)：290-293
(龙凤乐，郑文军，陈长风等. 温度、CO²分压、流速、pH值对X65管线钢CO²均匀腐蚀速率的影响规律 [J]. 腐蚀与防护，2005，26(7)：290-293)
[24] Zhang L，Hu L H，Sun J B, et al. Microstructure and properties of CO² corrosion resistant low Cr pipeline steels [J]. J. Mater. Eng.，2009，5：6-10
(张雷，胡丽华，孙建波等. 抗CO²腐蚀低Cr管线钢组织和性能研究 [J]. 材料工程，2009，5：6-10)
[25] Sun J B，Liu W，Chang W，et al. Characteristics and formation mechanism of corrosion scales on low chromium X65 steels in CO² environment [J]. Acta Metall. Sin.，2009，45(1)：84-90
(孙建波，柳伟，常炜等. 低铬X65管线钢CO²腐蚀产物膜的特征及形成机制 [J]. 金属学报，2009，45(1)：84-90)
[26] Yang X T，Zhou Q. A comparative analysis of the effects of CO²corrosion on banded pipeline steel structure in lower temperature areas [J]. J. Gansu Sci.，2005，17(2)：110-113
(杨新田，周琦. 管线钢带状组织对低温区CO²腐蚀行为影响的比较分析 [J]. 甘肃科学学报，2005，17(2)：110-113)
[27] Mi L T，Huang H，Huang R Q, et al. On process system to inject corrosion inhibitor [J]. Natural Gas Oil，1998，16(3)：20-30
(米力田，黄和，黄汝桥等. 缓蚀剂加注工艺系统研究 [J]. 天然气与石油，1998，16(3)：20-30)
[28] Mao X B. Study on the vapor phase inhibitor for leave unused equipment of refinery [D]. Zhejiang：Zhejiang University of Technology，2002
(毛信表. 炼油厂闲置设备保护用气相缓蚀剂的研究 [D]. 浙江：浙江工业大学，2002)
[29] Singer M，Ne?i? S. Top of the line corrosion in presence of acetic acid and carbon dioxide [A]. Corrosion/04 [C]. Houston：NACE，2004
[30] Chai C W，Lu M X，Zhang G A. Top of line corrosion and protection in wet gas environments [J]. Corros．Prot.，2007，28(4)：167-171
(柴成文，路民旭，张国安. 湿气管线的顶部腐蚀与防护对策 [J]. 腐蚀与防护，2007，28(4)：167-171)
[31] Zhang X Y，Di C，Lei L C. Carbon Dioxide Corrosion?and Control[M]. Beijing：Chemical Industry Press，2000
(张学元，邸超，雷良才. 二氧化碳腐蚀与控制 [M]. 北京：化学工业出版社，2000)
[32] Olsen S，Dugstad A. Corrosion under dewing conditions [A]. Corrosion/91 [C]. Houston：NACE，1991
[33] Vitse F，Khairul A，Gunaltun Y，et al. Semiempirical model for prediction of the top-of-the-line corrosion risk [A]. Corrosion/02 [C]. Houston：NACE，2002
[34] Vitse F，Gunaltun Y，Larrey De T D，et al. Mechanistic model for the prediction of top-of-the-line corrosion risk [A]. Corrosion/03 [C]. Houston：NACE，2003
[35] Gunaltun Y，Totalfinaelf. A new technique for the control of top of the line corrosion [A]. Corrosion/03 [C]. Houston：NACE，2003
[36] Li Y K. Electrochemical behavior research of metal corrosion under thin electrolyte lay [D]. Qingdao：Ocean University of China，2007
(李亚坤. 薄液层下金属电化学腐蚀行为研究 [D]. 青岛：中国海洋大学，2007)
[37] Wang L W，Li X G，Du C W，et al. Recent advances in local electrochemical measurement techniques and applications in corrosion research [J]. J. Chin. Soc. Corros. Prot.，2010，30(6)：498-504
(王力伟，李晓刚，杜翠薇等. 微区电化学测量技术进展及在腐蚀领域的应用 [J]. 中国腐蚀与防护学报，2010，30(6)：498-504)
[38] Ne?i? S. Key issues related to modeling of internal corrosion of oil and gas pipelines-A review [J]. Corros. Sci.，2007，49：4308-4338
[39] Sun Y H，Ne?i? S. A parametric study and modeling on localized CO² corrosion in horizontal wet gas flow [A]. Corrosion/04 [C]. Houston：NACE，2004
[40] Zhang G A，Cheng Y F. Localized corrosion of carbon steel in a CO²-saturated oilfield formation water [J]. Electrochim. Acta，2011，56:1676-1685
[41] Tang X，Cheng Y F. Localized dissolution electrochemistry at surface irregularities of pipeline steel [J]. Appl. Surf. Sci.，2008，254：5199-5205
[42] Visser E de，Hendriks C，Barrio M，et al. Dynamic CO² quality recommendations [J]. Int. J. Greenhouse Gas Contr.，2008，2：478-484
[43] Zhang H B，Liu M，Liu Y H，et al. Advances in the research of CO²corrosion in oil and gas field [J]. Oil Field Equip.，2008，37(4)：21-24
(张海宝，刘猛，刘永红等. 油气田CO²腐蚀研究进展 [J]. 石油矿场机械，2008，37(4)：21-24)
[44] Van Hunnkik E W J，Pots B F M，Hendriksen E L J A. The formation of protective FeCO³ corrosion product layers in CO² corrosion [A]. Corrosion/96 [C]. Houston：NACE，1996
[45] Pots B F M，Hendriksen E L J A. CO² corrosion scaling conditions-the special case of top-of-line corrosion in wet gas pipelines [A]. Corrosion/2000 [C]. Houston：NACE，2000
[46] Ne?i? S，Solvi G P，Enerhaug J. Comparison of the rotating cylinder and pipe flow tests for flow-sensitive carbon dioxide corrosion [J]. Corrosion，1995，51(10)：773-787
[47] Kermani M B，Smith L M. Translated by Wang X P. CO²Corrosion Control in Oil and Production-design Considerations [M]. Beijing：Petroleum Industry Press，2002
(克曼尼M B，史密斯L M. 王西平译. 油气生产中的CO²腐蚀控制——设计考虑因素 [M]. 北京：石油工业出版社，2002)
[48] Yao X. Prediction and protection of CO² corrosion of tubular goods in oil/gas wells [J]. Oil Drilling Prod. Technol.，1998，20(3)：44-49
(姚晓. CO²对油气井管材腐蚀的预测与防护 [J]. 石油钻采工艺，1998，20(3)：44-49)
[49] Chen C F，Lu M X，Zhao G X，et al. Characters of CO² corrosion scales on well tube steels N80 [J]. Acta Metall. Sin.，2002，38(4)：411-416
(陈长风，路民旭，赵国仙等. 油套管钢CO²腐蚀产物膜特征[J]. 金属学报，2002，38(4)：411-416)
[50] Mclntire G，Lippert J，Yudelson J. The effect of dissolved CO² and O² on the corrosion of iron [J]. Corrosion，1990，46(2)：91-94
[51] Ne?i? S，Postlethwaite J，S Olsen. An electrochemical model for prediction of CO² Corrosion [A]. Corrosion/95 [C]. Houston：NACE，1995
[52] Lopez D A，Perez T，Simison S N. The influence of microstructure and chemical composition of carbon and low alloy steels in CO² corrosion. A state-of-the-art appraisal [J]. Mater. Des.，2003，24：561-575
[53] Nyborg R. Overview of CO² corrosion models for wells and pipelines [A]. Corrosion/02 [C]. Houston：NACE，2002
[54] Sankara P，R Winston R，Waldemar I F，et al. Review of models to predict internal pitting corrosion [J]. Corros. Rev.，2006，24：173-230
[55] Xiang Y，Wang Z，Yang X X，et al. The upper limit of moisture content for supercritical CO² pipeline transport [J]. J. Supercritical Fluids，2012，3：1-39
[56] Ge G F．Economy and feasibility analysis on internal coating of pipeline [J]. Oil Gas Storage Transp.，2003，22(2)：54-57
(葛国防. 管道内涂层经济可行性分析 [J]. 油气储运，2003，22(2)：54-57)
[57] Ning K Y. The application of the composite lining in pipeline rehabilitation and pipeline construction [J]. Pet. Eng. Constr.，1995，2：36-39
(宁克远. 复合内衬技术在旧管线修复和新管线建设中的应用 [J]. 石油工程建设，1995，2：36-39)
[58] Liu W，Qian C W. The coating material used in internal coating for gas transmission [J]. Oil Gas Storage Transp.，2001，20(2)：13-19
(刘雯，钱成文. 输气管道内涂层用涂料 [J]. 油气储运，2001，20(2)：13-19)
[59] Jiang M，Zhi Y M，Liu W D, et al. Status and development of pipe line steel in China [J]. Shanghai Met., 2009, 31(6): 42-46
(姜敏，支玉明，刘卫东等. 我国管线钢的研发现状和发展趋势 [J]. 上海金属，2009，31(6)：42-46)

[1]	戴婷, 顾艳红, 高辉, 刘凯龙, 谢小辉, 焦向东. 水下摩擦螺柱焊接头在饱和CO₂中的电化学性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[4]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[5]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[6]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[7]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[8]	伊红伟, 胡慧慧, 陈长风, 贾小兰, 胡丽华. CO₂环境下油酸咪唑啉对X65钢异种金属焊缝电偶腐蚀的抑制作用研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 96-104.
[9]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[10]	袁玮,黄峰,甘丽君,戈方宇,刘静. 显微组织对X100管线钢氢致开裂及氢捕获行为影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 536-542.
[11]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[12]	史伟宁,杨树峰,李京社. 不锈钢中诱发局部腐蚀的贫Cr区研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 281-290.
[13]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[14]	史显波,杨春光,严伟,徐大可,闫茂成,单以银,杨柯. 管线钢的微生物腐蚀[J]. 中国腐蚀与防护学报, 2019, 39(1): 9-17.
[15]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.

Viewed

Full text

Abstract

Cited

Shared

Discussed