| 常用金属表面缓蚀自组装膜及其研究方法 |
| 王海人1，江 燕1,屈钧娥1,李文维1,陈凤1,张强2 |
1. 湖北大学材料科学与工程学院 武汉 430062；
2. 中国石油西南油气田分公司天然气研究院 成都 610213 |
|
| INHIBITIVE SELF-ASSEMBLED MONOLAYERS ON SURFACES OF COMMONLY-USED METALS AND RELATED RESEARCH METHODS |
| WANG Hairen1, JIANG Yan1, QU Jun'e1, LI Wenwei1, CHEN Feng1, ZHANG Qiang2 |
1. Faculty of Materials Science and Engineering, Hubei University, Wuhan 430062
2. Research Institute of Natural Gas Technology, Southwest Oil and Gas Field Branch, Petro China Ltd., Chengdu 610213 |
引用本文:
王海人,江 燕,屈钧娥,李文维,陈凤,张强. 常用金属表面缓蚀自组装膜及其研究方法[J]. 中国腐蚀与防护学报, 2012, 32(4): 273-284.
YU Hai-Ren,
JIANG Yan,
QUE Jun-E,
LI Wen-Wei,
CHEN Feng,
ZHANG Jiang.
INHIBITIVE SELF-ASSEMBLED MONOLAYERS ON SURFACES OF COMMONLY-USED METALS AND RELATED RESEARCH METHODS. J Chin Soc Corr Pro, 2012, 32(4): 273-284.
链接本文:
https://www.jcscp.org/CN/
或
https://www.jcscp.org/CN/Y2012/V32/I4/273
|
| [1] Zhai Y, Zhang J L, Li W H, et al. Preparation and application of the self-assembled monolayers [J]. Prog. Chem., 2004, 16(4): 477-484 (翟怡, 张金利, 李韦华等. 自组装单层膜的制备与应用[J]. 化学进展, 2004, 16(4): 477-484)[2] Zhang J L, Yang F, Zheng W J, et al. Self-assembly monolayers and their characterization[J]. Prog. Chem., 2005, 17(2): 203-208 (张俊苓, 杨芳, 郑文杰等. 自组装单分子膜及其表征方法[J]. 化学进展, 2005, 17(2): 203-208)[3] Messerschmidt C, Schwartz D K. Growth mechanisms of octadecylphosphonic acid self-assembled monolayers on sapphire (corundum): Evidence for a quasi-equilibrium triple point[J]. Langmuir, 2000, 17(2): 462-467[4] Yang X G, Chen S H, Ma H Y, et al. Inhibitive self-assembled monolayers on metal surface [J]. Prog. Chem., 2003, 15(2): 123-128 (杨学耕, 陈慎豪, 马厚义等. 金属表面自组装缓蚀功能分子膜[J]. 化学进展, 2003, 15(2): 123-128)[5] Yang S R, Ren S L, Zhang J Y, et al. Structure and self-assembly mechanism of self -assembled monolayers[J]. Chem. J. Chin. Univ., 2001, 22(3): 470-476 (杨生荣, 任嗣利, 张俊彦等. 自组装单分子膜的结构及其自组装机理[J]. 高等学校化学学报, 2001, 22(3): 470-476)[6] Bigelow W C, Pickett D L, Zisman W A. Oleophobic monolayers: I. Films adsorbed from solution in non-polar liquids[J]. J. Colloid Sci., 1946, 1(6): 513-538[7] Nuzzo R G, Allara D L. Adsorption of bifunctional organic disulfides on gold surfaces[J]. J. Am. Chem. Soc., 1983, 105(13): 4481-4483[8] Laibinis P E, Whitesides G M. Self-assembled monolayers of n-alkanethiolates on copper are barrier films that protect the metal against oxidation by air[J]. J. Am. Chem. Soc., 1992, 114 (23): 9022-9028[9] Itoh M, Nishihara H, Aramaki K. Preparation and evaluation of two-dimensional polymer films by chemical modification of an alkanethiol self-assembled monolayer for protection of copper against corrosion[J]. J. Electrochem. Soc., 1995, 142(11): 3696-3704[10] Haneda R, Nishihara H, Aramaki K. Chemical modification of an alkanethiol self-assembled layer to prevent corrosion of copper [J]. J. Electrochem. Soc., 1997, 144(4): 1215-1221[11] Haneda R, Aramaki K. Protection of copper corrosion by an ultrathin two-dimensional polymer film of alkanethiol monolayer[J]. J. Electrochem. Soc., 1998, 145(6): 1856-1861[12] Haneda R, Aramaki K. Protective films on copper by multistep modification of an alkanethiol monolayer with chlorosilanes and alkanediol[J]. J. Electrochem. Soc., 1998, 145(8): 2786-2791[13] Ma H Y, Yang C, Chen S H, et al. Electrochemical investigation of dynamic interfacial processes at 1-octadecanethiol-modified copper electrodes in halide-containing solutions[J]. Electrochim. Acta, 2003, 48(28), 4277-4289[14] Ma H Y, Yang C, Yin B S, et al. Electrochemical characterization of copper surface modified by n-alkanethiols in chloride-containing solutions[J]. Appl. Surf. Sci., 2003, 218 (1-4): 144-154[15] Fan H, Li S, Zhao Z, et al. Inhibition of brass corrosion in sodium chloride solutions by self-assembled silane films[J]. Corros. Sci., 2011, 53(12), 4273-4281[16] Caprioli F, Decker F, Castro V D. Durable Cu corrosion inhibition in acidic solution by SAMs of Benzenethiol[J]. J. Electroanal. Chem., 2011, 657 (1-2), 192-195[17] Quan Z, Chen S H, Li Y, et al. Adsorption behaviour of Schiff base and corrosion protection of resulting films to copper substrate[J]. Corros. Sci., 2002, 44(4): 703-715[18] Guo W J, Chen S H, Huang B D, et al. Protection of self-assembled monolayers formed from triethyl phosphate and mixed self-assembled monolayers from triethyl phosphate and cetyltrimethyl ammonium bromide for copper against corrosion[J]. Electrochim. Acta, 2006, 52(1): 108-113[19] Appa Rao B V, Iqbal M Y, Sreedhar B. Self-assembled monolayer of 2-(octadecylthio)benzothiazole for corrosion protection of copper[J]. Corros. Sci., 2009, 51(6): 1441-1452[20] Appa Rao B V, Iqbal M Y, Sreedhar B. Electrochemical and surface analytical studies of the self-assembled monolayer of 5-methoxy-2-(octadecylthio)benzimidazole in corrosion protection of copper[J]. Electrochim. Acta, 2010, 55(3): 620-631[21] Liao Q Q, Yue Z W, Yang D, et al. Inhibition of copper corrosion in sodium chloride solution by the self-assembled monolayer of sodium diethyldithiocarbamate[J]. Corros. Sci., 2011, 53(5), 1999-2005[22] Wang C T, Chen S H. Influence of thiourea molecular structure on its self-assembled ability onto copper surface [J]. Acta Chim. Sin., 2007, 65(5): 390-394 (王春涛, 陈慎豪. 分子结构对硫脲类化合物在铜表面自组装能力的影响[J]. 化学学报, 2007, 65(5): 390-394)[23] Simbeck T, Thomaier S, Stock C, et al. Measurement of adsorption kinetics of benzotriazole on copper surfaces via impedance scanning quartz crystal microbalance studies[J]. Electrochem. Commun., 2011, 13 (8): 803-805[24] Qin T T, Li J, Luo H Q, et al. Corrosion inhibition of copper by 2,5-dimercapto-1,3,4-thiadiazole monolayer in acidic solution[J]. Corros. Sci., 2011, 53(3): 1072-1078[25] Hao C, Yin R H, Wan Z Y, et al. Electrochemical and photoelectrochemical study of the self-assembled monolayer phytic acid on cupronickel B30[J]. Corros. Sci., 2008, 50(12): 3527-3533[26] Ma H F. Corrosion inhibition of copper by self-assembled polyvinylpyrroidone film[J]. J. Mater. Prot., 2010, 43(1): 57-59 (马洪芳. 聚乙烯吡咯烷酮自组装膜对铜的缓蚀作用[J]. 材料保护, 2010, 43(1): 57-59)[27] Zhang Z, Chen S, Ren H, et al. Protection of iron ag-ainst corrosion by coverage with Au nanoparticles and n-hexylthiol mixed films[J]. Appl. Surf. Sci., 2009, 255(9): 4950-4954[28] Zhang D Q, He X M, Cai Q R, et al. pH and iodide ion effect on corrosion inhibition of histidine self-assembled monolayer on copper[J]. Thin Solid Films, 2010, 518(10), 2745-2749[29] Yue Y Z, Sang S B, Tang A D, et al. Inhibition action of self-assembled monolayers of P-hydroxybenzoic acid on copper[J]. Guangzhou Chem. Ind. Technol., 2011, 39(3): 78-81 (岳艳枝, 桑商斌, 唐爱东等. 对羟基苯甲酸自组装膜对铜的缓蚀作用[J]. 广州化工, 2011, 39(3): 78-81)[30] Xiang Y G, Wang C T, Wang J, et al. The inhibition effects of N,N-dimethylformanmide self-assembled films for copper. [J] Plat. Finish., 2011, 33(1): 35-37 (相永刚, 王春涛, 王晶等. N,N-二甲基甲酰胺自组装膜对铜的缓蚀作用[J]. 电镀与精饰, 2011,33 (1): 35-37)[31] Volmer-Uebing M, Stratmann M. A surface analytical and an electrochemical study of iron surfaces modified by thiols[J]. Appl. Surf. Sci., 1992, 55(1): 19-35[32] Nozawa K, Nishihara H, Aramaki K. Chemical modification of alkanethiol monolayers for protecting iron against corrosion[J]. Corros. Sci., 1997, 39(9): 1625-1639[33] Wang J, Li D G, Yu X J, et al. SAMs of dodecyl mercaptan and its corrosion protection in iron surface[J]. J. Chin. Soc. Corros. Prot., 2010, 30(3): 207-212 (王静, 李德刚, 于先进等. 十二烷基硫醇在Fe表面自组装成膜及对其的腐蚀保护[J]. 中国腐蚀与防护学报, 2010, 30(3): 207-212)[34] Wang J. The self-assembled monolayers of N-and T- dodecanethiol on the surface of iron[D]. Master Degree Thesis, Zibo: Shandong University of Technology, 2009 (王静. 正、叔十二烷基硫醇在铁上的自组装[D]. 硕士学位论文, 淄博: 山东理工大学, 2009)[35] Aramaki K, Shimura T. Self-assembled monolayers of carboxylate ions on passivated iron for preventing passive film breakdown[J]. Corros. Sci., 2004, 46(2): 313-328[36] Aramaki K, Shimura T. Prevention of passive film breakdown and corrosion of iron in 0.1 M KClO4 with and without Cl- by covering with an ultrathin two-dimensional polymer coating and healing treatment in 0.1 M NaNO3[J]. Corros. Sci., 2010, 52(9): 2766-2772[37] Aramaki K, Shimura T. Protection of passivated iron against corrosion in a 0.1 M NaNO3 solution by coverage with an ultrathin polymer coating of carboxylate SAM[J]. Corros. Sci., 2009, 51(9): 1887-1893[38] Aramaki K, Shimura T. An ultrathin polymer coating of carboxylate self-assembled monolayer adsorbed on passivated iron to prevent iron corrosion in 0.1 M Na2SO4[J]. Corros. Sci., 2010, 52(1): 1-6[39] Ramachandran S,Tsai B L, Blanco M, et al. Self-assembled monolayer mechanism for corrosion inhibition of iron by imidazolines[J]. Langmuir, 1996, 12(26): 6419-6428[40] Liu X Y. Mater. Rev., 2008, 22(6): 152 (刘秀玉. 铁、不锈钢表面自组装膜的表征及其电化学研究[J]. 材料导报, 2008, 22(6): 152)[41] Yang H, Yang Y, Yang Y, et al. Formation of inositol hexaphosphate monolayers at the copper surface from a Na-salt of phytic acid solution studied by in situ surface enhanced Raman scattering spectroscopy, Raman mapping and polarization measurement[J]. Anal. Chim. Acta, 2005, 548(1-2): 159-165[42] Guo W J. Study of the experimental methods of self-assembled films of phosphates on copper or iron surface for corrosion inhibition[D]. PhD thesis, Jinan: Shandong University, 2007 (郭文娟. 铜、铁表面组装膦酸酯类缓蚀功能分子膜实验技术的研究[D]. 博士学位论文, 济南: 山东大学, 2007)[43] Paszternak A, Felhosi I, Paszti Z, et al. Surface analytical characterization of passive iron surface modified by alkyl-phosphonic acid layers[J]. Electrochim. Acta, 2010, 55(3), 804-812[44] Nozawa K, Aramaki K. One-and two-dimensional polymer films of modified alkanethiol monolayers for preventing iron from corrosion[J]. Corros. Sci., 1999, 41(1): 57-73[45] Shimura T, Aramaki K. Additional modification to two-dimensional polymer films of a hydroxymethylbenzene self-assembled monolayer with alkyltriethoxysilanes for enhancing the protective abilities against iron corrosion[J]. Corros. Sci., 2008, 50(2): 596-604[46] Aramaki K, Shimura T. Improvement of healing treatment with NaNO3 for a passivated iron electrode covered with an ultrathin polymer coating to prevent iron corrosion in some solutions containing aggressive anions[J]. Corros. Sci., 2011, 53(12), 4152-4158[47] Feng Y Y, Chen S H, Zhou J J, et al. Corrosion inhibition of self-assembled films on iron by electrochemical impedance spectroscopy [J]Electrochemistry, 2008, 14(3): 343-346 (冯媛媛, 陈慎豪, 周娟娟等. 铁表面自组装缓蚀功能膜的电化学阻抗谱研究[J]. 电化学, 2008, 14(3): 343-346)[48] Wang D, Ni Y, Huo Q, et al. Self-assembled monolayer and multilayer thin films on aluminum 2024-T3 substrates and their corrosion resistance study[J]. Thin Solid Films, 2005, 471(1-2): 177-185[49] Cecchetto L, Denoyelle A, Delabouglise D, et al. A silane pre-treatment for improving corrosion resistance performances of emeraldine base-coated aluminium samples in neutral environment[J]. Appl. Surf. Sci., 2008, 254(6): 1736-1743[50] De Rose J A, Hoque E, Bhushan B, et al. Characterization of perfluorodecanoate self-assembled monolayers on aluminum and comparison of stability with phosphonate and siloxy self-assembled monolayers[J]. Surf. Sci., 2008, 602(7): 1360-1367[51] Kim J, Wong P C, Wong K C, et al. Adsorption of BTSE and γ-GPS organosilanes on different microstructural regions of 7075-T6 aluminum alloy[J]. Appl. Surf. Sci., 2007, 253(6): 3133-3143[52] Susac D, Sun X, Mitchell K A R. Adsorption of BTSE and γ-GPS organosilanes on different microstructural regions of 2024-T3 aluminum alloy[J]. Appl. Surf. Sci., 2003, 207(1-4): 40-50[53] Hintze P E, Calle L M. Electrochemical properties and corrosion protection of organosilane self-assembled monolayers on aluminum 2024-T3[J]. Electrochim. Acta, 2006, 51(8-9): 1761-1766[54] Guo Z C, Wang Y F, Wang R M. Corrosion resistance of self-assembled monolayer on Al-alloy surface [J]. Mater. Prot., 2007, 40(7): 1-4 (郭增昌, 王云芳, 王汝敏. 铝合金表面自组装膜层的表征及耐蚀性研究[J]. 材料保护, 2007, 40(7): 1-4)[55] Liakos I L, Newman R C, McAlpine E, et al. Study of the resistance of SAMs on aluminium to acidic and basic solutions using dynamic contact angle measurement[J]. Langmuir, 2006, 23 (3): 995-999[56] Wapner K, Stratmann M, Grundmeier G. Structure and stability of adhesion promoting aminopropyl phosphonate layers at polymer/aluminium oxide interfaces[J]. Int. J. Adhes. Adhes., 2007, 28 (1-2): 59-70[57] Reis F M, de Melo H G, Costa I. EIS investigation on Al 5052 alloy surface preparation for self-assembling monolayer[J]. Electrochim. Acta ,2006, 51(8-9): 1780-1788[58] Wang H R, Qu J E, Zhang Q, et al. The adsorption and corrosion inhibition behavior of TDPA self-assembled monolayers on the surface of aluminum alloy [J]. Surf. Technol., 2011, 40(1): 40-43 (王海人, 屈钧娥, 张强等. 膦酸自组装膜在铝合金表面的吸附及缓蚀行为[J]. 表面技术, 2011, 40(1): 40-43)[59] Allara D L, Nuzzo R G. Spontaneously organized molecular assemblies. 1. Formation, dynamics, and physical properties of n-alkanoic acids adsorbed from solution on an oxidized aluminum surface[J]. Langmuir, 1985, 1(1): 45-52[60] Taylor C E, Schwartz D K. Octadecanoic acid self-assembled monolayer growth at sapphire surfaces[J]. Langmuir, 2003, 19 (7): 2665-2672[61] Foster T T, Alexander M R, Leggett G J, et al. Friction force microscopy of alkylphosphonic acid and carboxylic acids adsorbed on the native oxide of aluminum[J]. Langmuir, 2006, 22(22): 9254-9259[62] Yong Z Y, Liu Y L, Li Z. Self-assembled monolecular films of oleic imidazoline on magnesium alloy AZ91D for corrosion protection[J]. Corros. Sci. Prot. Technol., 2006, 18 (2): 79-82 (雍止一, 刘娅莉, 李智. 咪唑啉自组装单分子膜在镁合金AZ91D表面的防腐蚀研究[J]. 腐蚀科学与防护技术, 2006, 18(2): 79-82)[63] Liu Y, Yu Z, Zhou S, et al. Self-assembled monolayers on magnesium alloy surfaces from carboxylate ions[J]. Appl. Surf. Sci., 2006, 252(10): 3818-3827[64] Ishizaki T, Teshima K, Masuda Y, et al. Liquid phase formation of alkyl- and perfluoro-phosphonic acid derived monolayers on magnesium alloy AZ31 and their chemical properties[J]. J. Colloid Interface Sci., 2011, 360(1): 280-288[65] Berger F, Delhalle J, Mekhalif Z. Self-assembled bilayers based on organothiol and organotrimethoxysilane on zinc platform[J]. Appl. Surf. Sci., 2010, 256(23): 7131-7137[66] Qiao J S, Luo H Q, Li M, et al. Corrosion inhibition effect of uric acid self-assembled film to nickel[J]. J. Chin. Soc. Corros. Prot., 2009, 29(2): 145-148 (乔建仙, 罗红群, 李明等. 尿酸自组装膜对镍缓蚀行为的影响[J]. 中国腐蚀与防护学报, 2009, 29(2): 145-148)[67] Blajiev O L, Ithurbide A, Hubin A, et al. XPS study of the assembling morphology of 3-hydroxy-3-phosphono-butiric acid tert-butyl ester on variously pretreated Al surfaces[J]. Prog. Org. Coat., 2008, 63(3): 272-281[68] Sung M M, Sung K, Kim C G, et al. Self-assembled monolayers of alkanethiols on oxidized copper surfaces[J]. J. Phys. Chem., 2000, 104B(10): 2273-2277[69] Fonder G, Minet I, Volcke C, et al. Anchoring of alkylphosphonic derivatives molecules on copper oxide surfaces[J]. Appl. Surf. Sci., 2011, 257(14), 6300-6307[70] Ishizaki T, Okido M, Masuda Y, et al. Corrosion resistant performances of alkanoic and phosphonic acids derived self-assembled monolayers on magnesium alloy AZ31 by vapor-phase method[J]. Langmuir, 2011, 27(10): 6009-6017[71] Ishizaki T, Sakamoto M. Facile formation of biomimetic color-tuned superhydrophobic magnesium alloy with corrosion resistance[J]. Langmuir, 2011, 27(6): 2375-2381[72] Ding Y M, Xu C C, Wang J L. Comparative study of volatile corrosion inhibitors (VCI) for bronze cultural relics[J]. J. Beijing Univ. Chem. Technol., 2006, 33(2): 68-71 (丁艳梅, 许淳淳, 王菊琳. 铜器文物用气相缓蚀剂的研究[J]. 北京化工大学学报, 2006, 33(2): 68-71)[73] Ron H, Cohen H, Matlis S, et al. Self-assembled monolayers on oxidized metals. 4. Superior n-alkanethiol monolayers on copper[J]. J. Phys. Chem., 1998, 102B(49): 9861-9869[74] Wang P, Liang C, Wu B, et al. Protection of copper corrosion by modification of dodecanethiol self-assembled monolayers prepared in aqueous micellar solution[J]. Electrochim. Acta, 2010, 55 (3), 878-883[75] Fonder G, Laffineur F, Delhalle J, et al. Alkanethiol-oxidized copper interface: The critical influence of concentration[J]. J. Colloid Interface Sci., 2008, 326(2), 333-338[76] Spori D M, Venkataraman N V, Tosatti S G P, et al. Influence of alkyl chain length on phosphate self-assembled monolayers[J]. Langmuir, 2007, 23(15): 8053-8060[77] Hoque E, DeRose J A, Hoffmann P, et al. Phosphonate self-assembled monolayers on aluminum surfaces[J]. J. Chem. Phys., 2006, 124(17): 174710-174716[78] Hoque E, DeRose J A, Kulik G, et al. Alkylphosphonate modified aluminum oxide surfaces[J]. J. Phys. Chem. B, 2006, 110(22): 10855-10861[79] Zhu L. Researching methods for inhibition mechanism of corrosion inhibitors[J]. Corros. Prot., 1999, 20(7): 300-302 (朱苓. 缓蚀剂缓蚀作用的研究方法[J]. 腐蚀与防护, 1999, 20(7): 301-302)[80] Gao Y, Liu H M. Application development of electrochemical impedance spectroscopy in researching corrosion inhibitor[J]. J. Chem. Ind. Eng., 2007, 28(5): 36-39 (高岩, 刘鹤鸣. 电化学阻抗谱在缓蚀剂研究中的应用进展[J]. 化学工业与工程技术, 2007, 28(5): 36-39)[81] Tan Y S, Srinivasan M P, Pehkonen S O, et al. Effects of ring substituents on the protective properties of self-assembled benzenethiols on copper[J]. Corros. Sci., 2006, 48(4): 840-862[82] Frignani A, Zucchi F, Trabanelli G, et al. Protective action towards aluminium corrosion by silanes with a long aliphatic chain[J]. Corros. Sci., 2006, 48(8): 2258-2273[83] Li D. Yu X, Dong Y. The different self-assembled way of n- and t-dodecyl mercaptan on the surface of copper[J]. Appl. Surf. Sci., 2007, 253(9): 4182-4187[84] Song S Z. Research Methods on Corrosion Electrochemistry[M]. Beijing:Chemical Industry Press: 1988: 1 (宋诗哲. 腐蚀电化学研究方法[M]. 北京: 化学工业出版社, 1988: 1)[85] Liao Q Q, Yue Z W, Zhu Z W, et al. Corrosion inhibition effect of self-assembled monolayers of ammonium pyrrolidine dithiocarbamate on copper[J]. Acta Phys. Chim. Sin., 2009, 25(8): 1655-1661 (廖强强, 岳忠文, 朱忠伟等. 吡咯烷二硫代氨基甲酸铵自组装膜对铜的缓蚀作用[J]. 物理化学学报, 2009, 25(8): 1655-1661)[86] Ishizaki T, Teshima K, Masuda Y, et al. Liquid phase formation of alkyl- and perfluoro-phosphonic acid derived monolayers on magnesium alloy AZ31 and their chemical properties[J]. J. Colloid Interface Sci., 2011, 360(1): 280-288[87] Sinapi F, Deroubaix S, Pirlot C, et al. Electrochemical evaluation of the corrosion protection of bi-dimensional organic films self-assembled onto brass[J]. Electrochim. Acta, 2004, 49 (17-18): 2987-2996[88] Sinapi F, Delhalle J, Mekhalif Z. XPS and electrochemical evaluation of two-dimensional organic films obtained by chemical modification of self-assembled monolayers of (3-mercaptopropyl)trimethoxysilane on copper surfaces[J]. Mater. Sci. Eng., 2002, C22(2): 345-353[89] Sinapi F, Lejeune I, Delhalle J, et al. Comparative protective abilities of organothiols SAM coatings applied to copper dissolution in aqueous environments[J]. Electrochim. Acta, 2007, 52(16): 5182-5190[90] Deng H, Nanjo H, Qian P, et al. Corrosion prevention of iron with novel organic inhibitor of hydroxamic acid and UV irradiation[J]. Electrochim. Acta, 2008, 53(6): 2972-2983[91] Xu Q J, Wan Z Y, Yin R H, et al. Inhibition action of self-assembled monolayers of 3-amino-1,2,3-triazole on brass[J]. Acta Phys. Chim. Sin., 2008, 24(1): 115-120 (徐群杰,万宗跃,印仁和等. 3-氨基-1,2,4-三氮唑对铜的缓蚀性能和吸附行为[J]. 物理化学学报, 2008, 24(1): 115-120)[92] Alagta A, Felhosi I, Bertoti I, et al. Corrosion protection properties of hydroxamic acid self-assembled monolayer on carbon steel[J]. Corros. Sci., 2008, 50 (6): 1644-1649[93] Chen H, Wang J, Huo Q. Self-assembled monolayer of 3-aminopropyltrimethoxysilane for improved adhesion between aluminum alloy substrate and polyurethane coating[J]. Thin Solid Films, 2007, 515 (18): 7181-7189[94] Fonder G, Delhalle J, Essahli M, et al. Anchoring of sulfur-containing alkylphosphonic and semifluorinated alkylphosphonic molecules on a polycrystalline aluminum substrate[J]. Surf. Interface Anal., 2008, 40(2): 85-96[95] Hofer R, Textor M, Spencer N D. Alkyl phosphate monolayers, self-assembled from aqueous solution onto metal oxide surfaces[J]. Langmuir, 2001, 17(13): 4014-4020[96] Carbonell L, Whelan C M, Kinsella M, et al. A thermal stability study of alkane and aromatic thiolate self-assembled monolayers on copper surfaces[J]. Superlattices Microstruct., 2004, 36(1-3): 149-160[97] Bram C, Jung C, Stratmann M. Self assembled molecular monolayers on oxidized inhomogeneous aluminum surfaces[J]. Fresenius J. Anal. Chem., 1997, 358(1-2): 108-111[98] Cabral A M, Duarte R G, Montemor M F, et al. A comparative study on the corrosion resistance of AA2024-T3 substrates pre-treated with different silane solutions: Composition of the films formed[J]. Prog. Org. Coat., 2005, 54(4): 322-331[99] Pellerite M J, Dunbar T D, Boardman L D, et al. Effects of fluorination on self-assembled monolayer formation from alkanephosphonic acids on aluminum: kinetics and structure[J]. J. Phys. Chem., 2003, 107B(42): 11726-11736[100] Chen M A, Xie X, Qi H Y, et al. Characterization of self-assembled bis-[trithoxysilypropyl] tetrasulfide silane films on surface of 2A12-T6 aluminum alloy[J]. Acta Phys. Chim. Sin., 2006, 22(8): 1025-1029 (陈明安,谢 玄,戚海英等. 2A12-T6铝合金表面双-(γ-三乙氧基硅丙基)四硫化物薄膜的特性[J]. 物理化学学报, 2006, 22(8): 1025-1029)[101] Ding X Y, Wu D Y, Yang Z L, et al. Some progress in mechanistic studies on surface-enhanced Raman scattering[J]. Chem. J. Chin. Univ., 2008, 29(12): 2569-2581 (丁松园, 吴德印, 杨志林等. 表面增强拉曼散射增强机理的部分研究进展[J]. 高等学校化学学报, 2008, 29(12): 2569-2581)[102] Houssiau L, Bertrand P. TOF-SIMS study of alkanethiol adsorption and ordering on gold[J]. Appl. Surf. Sci., 2001, 175-176: 399-406[103] Petrovic Z, Metikos-Hukovic M, Babic R. Modification of copper with self-assembled organic coatings[J]. Prog. Org. Coat., 2008, 61(1): 1-6[104] Saito N, Lee S H, Takahiro I, et al. Surface-potential reversibility of an amino-terminated self-assembled monolayer based on nanoprobe chemistry[J]. J. Phys. Chem. B, 2005, 109(23): 11602-11605[105] Ishizaki T, Masuda Y, Sakamoto M. Corrosion resistance and durability of superhydrophobic surface formed on magnesium alloy coated with nanostructured cerium oxide film and fluoroalkylsilane molecules in corrosive NaCl aqueous solution[J]. Langmuir, 2011, 27(8): 4780-4788[106] Kong D S, Yuan S L, Sun Y X, et al. Self-assembled monolayer of o-aminothiophenol on Fe(110) surface: a combined study by electrochemistry, in situ STM, and molecular simulations[J]. Surf. Sci., 2004, 573(2): 272-283[107] Wintjes N, Lobo-Checa J, Hornung J, et al. Two-dimensional phase behavior of a bimolecular porphyrin system at the soli-vacuum interface[J]. J. Am. Chem. Soc., 2010, 132 (21): 7306-7311[108] Han M J, Xu Q M, Wan L J, et al. Adlayer structures of organic molecules with different functional groups on Cu(111) in solution[J]. J. Phys. Chem., 2002, 106B(43): 11272-11276[109] Raman A, Dubey M, Gouzman I, et al. Formation of self-assembled monolayers of alkylphosphonic acid on the native oxide surface of SS316L[J]. Langmuir, 2006, 22(15): 6469-6472[110] Raman A, Gawalt E S. Self-assembled monolayers of alkanoic acids on the native oxide surface of SS316L by solution deposition[J]. Langmuir, 2007, 23(5): 2284-2288[111] Zhang B, Kong T, Xu W, et al. Surface functionalization of zinc oxide by carboxyalkylphosphonic acid self-assembled monolayers[J]. Langmuir, 2010, 26(6): 4514-4522[112] Brukman M J, Oncins G, Dunbar T D, et al. Nanotribological properties of alkanephosphonic acid self-assembled monolayers on aluminum oxide: effects of fluorination and substrate crystallinity[J]. Langmuir, 2006, 22(9): 3988-3998[113] Hoque E, De Rose J A, Hoffmann P, et al. Alkylperfluorosilane self-assembled monolayers on aluminum: a comparison with alkylphosphonate self-assembled monolayers[J]. J. Phys. Chem., 2007, 111C(10): 3956-3962[114] Hoque E, De Rose J A, Bhushan B, et al. Low adhesion, non-wetting phosphonate self-assembled monolayer films formed on copper oxide surfaces[J]. Ultramicroscopy, 2009, 109(8): 1015-1022[115] Qu J E, Guo X P, Zhang J Z, et al. Electrochemical behavior and micro adhesive force characteristic of corrosion inhibition film[J].Acta Phys. Chim. Sin., 2008, 24(8): 1507-1512 (屈钧娥, 郭兴蓬, 张金枝等. 缓蚀膜电化学行为与微观粘附力特征[J]. 物理化学学报, 2008, 24(8): 1507-1512)[116] Qu J E, Guo X, Chen Z. Adsorption behavior of dodecylamine on copper-nickel alloy surface in NaCl solutions studied by electrochemical methods and AFM [J]. Mater. Chem. Phys., 2005, 93(2-3): 388-394[117] Patois T, Et Taouil A, Lallemand F, et al. Microtribological and corrosion behaviors of 1H,1H,2H,2H-perfluorodecanethiol self-assembled films on copper surfaces[J]. Surf. Coat. Technol., 2010, 205(7): 2511-2517[118] Feng Y, Chen S, Zhang H, et al. Characterization of iron surface modified by 2-mercaptobenzothiazole self-assembled monolayers[J]. Appl. Surf. Sci., 2006, 253(5): 2812-2819[119] Giza M, Thissen P, Grundmeier G. Adsorption kinetics of organophosphonic acids on plasma-modified oxide-covered aluminum surfaces[J]. Langmuir, 2008, 24(16): 8688-8694 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|