玻璃纤维/环氧复合涂层耐腐蚀性能研究
郝永胜,刘福春,史洪微,韩恩厚
中国科学院金属研究所 金属腐蚀与防护国家重点实验室 沈阳 110016
ANTICORROSION PROPERTIES OF EPOXY/GLASS FIBER COATINGS
HAO Yongsheng, LIU Fuchun, SHI Hongwei, HAN EnHou
State Key Laboratory for Metallic Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
全文: PDF(1926 KB)  
摘要: 研究了超细玻璃纤维对双酚A型(E44)和双酚F型(DER354)环氧树脂涂层体系力学性能和耐腐蚀性能的影响。通过盐雾试验和电化学阻抗谱(EIS)研究了涂层的耐腐蚀性。结果表明在双酚A和双酚F环氧树脂组成的涂料体系中,双酚A环氧树脂能够提高涂层的硬度,而双酚 F环氧树脂能够提高涂层的耐腐蚀性。
关键词 超细玻璃纤维电化学阻抗谱耐腐蚀    
Abstract:This paper focuses on the influence of ultra-fine glass fiber on the coating properties. Diglycidyl ether of bisphenol-A and diglycidyl ether of bisphenol-F epoxy resins were used as film former. Salt spray test and electrochemical impedance spectroscopy (EIS) were employed to characterize the anticorrosion properties of the coatings. Experimental results indicate that the diglycidyl ether of bisphenol-A epoxy resin can improve the coating hardness, while the diglycidyl ether of bisphenol-F epoxy resin has better anticorrosion properties.
Key wordsultra-fine glass fiber    EIS    anticorrosion
收稿日期: 2010-08-12     
ZTFLH: 

TG172

 
基金资助:

国家科技支撑计划项目(2007BAB27B02-02,2009BAE70B02)资助

通讯作者: 刘福春     E-mail: fcliu@imr.ac.cn
Corresponding author: LIU Fuchun     E-mail: fcliu@imr.ac.cn
作者简介: 郝永胜,男,1979年生,博士生,研究方向为海洋防腐蚀涂料

引用本文:

郝永胜,刘福春,史洪微,韩恩厚. 玻璃纤维/环氧复合涂层耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2011, 31(6): 426-430.
HAO Yong-Qing. ANTICORROSION PROPERTIES OF EPOXY/GLASS FIBER COATINGS. J Chin Soc Corr Pro, 2011, 31(6): 426-430.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2011/V31/I6/426

[1] Sjoren A, Joffe R, Berglund L, et al, Effects of fibre coating (size) on properties of glass fibre/vinyl ester composites [J]. Composites, 1999, 30A: S1009-S1015

[2] Ben Amor I, Rekik H, Kaddami H, et al, Studies of dielectric relaxation in natural fiber-polymer composites [J]. J.Electrostat. 2009, 67: 717-722

[3] Cantwell W J, Morton J. The impact resistance of composite materials-a review [J]. Composites, 1991, 22: 347-362

[4] Schutte C L. Enperimental durability of glass-fiber composites [J]. Mater. Sci. Eng., 1994, R13: 265-324

[5] Reis J M L. Ferreira A J M. Fracture behavior of glass fiber reinforced polymer concrete [J]. Polym. Test, 2003, 22:149-153

[6] Thomason J L. The interface region in glass fibre-reinforced epoxy resin composites: 3. Characterization of fibre surface coatings and the interphase [J]. Composites, 1995, 26:487-498

[7] Wei W, Cheng G X, Zhang D S. Investigation of unidirectional glass fiber reinforced epoxy resin composite [J]. J.Xi'an Jiaotong Univ., 1999, 33(8): 108-110

    (韦玮, 程光旭,张东山, 玻璃纤维增强环氧树脂单向复合材料的研究 [J].西安交通大学学报. 1999, 33(8): 108-110)

[8] Zheng L, Liao G X, Xu Y J, et al. Properties of continuous glass fiber composites based on PEESK blends [J]. Poly. Mater. Sci.Eng., 2009, 25: 48-51

    (郑亮, 廖功雄, 徐亚娟等,连续玻璃纤维增强PPESK共混树脂基复合材料的性能 [J].高分子材料科学与工程, 2009, 25: 48-51)

[9] Zhuang H, Ren P, Liu X X, et al. Influence of matrix resin on mechanical properties of LGF-PP [J]. China Synthetic Resin Plasti., 2007, (24): 17-19

    (庄辉, 任璞, 刘学习等,基体树脂对长玻璃纤维增强力学性能的影响 [J]. 合成树脂与塑料, 2007,24: 17-19)

[10] Yang Z Q, Wu F Q, Lian W,et al. Research on fatigue properties of glass fiber reinforced resin composite [J]. Fiber Glass, 2008, 5: 19-23.

     (杨忠清, 吴富强, 廉伟等,玻璃纤维增强树脂基复合材料疲劳性能的试验研究 [J]. 玻璃纤维, 2008,(5): 19-23)

[11] Zhan M S, Liu D S. Acid rain cycling aging property and mechanism unindirectional glass fiber reinforced epoxy composites [J]. Fiber Reinforced Plastics/Composites. 2007, 5: 28-32.

     (詹茂盛, 刘德顺, 玻纤增强环氧树脂复合材料的酸雨循环老化性能与机理[J]. 玻璃钢/复合材料, 2007, 5: 28-32)

[12] Yan W, Guo J B, Xue B, et al. Effect of epoxy resin on the properties of glass fiber reinforced PA6 [J]. Plastics. 2009,38: 13-15.

     (严伟, 郭建兵, 薛斌等,环氧树脂对玻纤增强PA6力学性能的影响 [J]. 塑料, 2009, 38: 13-15)

[13] Song Y J, Huang L J, Zhu P, et al. Friction and wear of coupling agent treated glass fiber modified composites [J].Mater.Eng., 2009, (2): 58-64

     (宋艳江, 黄丽坚, 朱鹏等,偶联剂处理玻璃纤维改性聚酰亚胺摩擦磨损性能研究 [J]. 材料工程, 2009,(2): 58-64)

[14] Wu W L, Wang J. Study and development on the interface modification of fiber in the reinforced epoxy [J]. J. Xi'an Polytech. Univ., 2009,(23): 149-154.

     (武卫莉, 王晶,增强树脂用纤维表面处理研究进展 [J]. 西安工程大学学报,2009,(23):149-154)

[15] Laura D M, Keskkula H, Barlow J W, et al, Effect of glass fiber surface chemistry on the mechanical properties of glass fiber reinforced, rubber-toughened nylon 6 [J]. Polym, 2002, 43:4673-4687\par
[1] 韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[2] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4] 杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al2O3复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[5] 赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[6] 肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[7] 欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[8] 史昆玉,张进中,张毅,万毅. Nb2N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[9] 王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[10] 达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[11] 冯旭,费敬银,李倍,张嫚,郭琪琪. 组分调制Ni/Cr多层膜合金化制备Ni-Cr合金覆盖层的耐腐蚀特性[J]. 中国腐蚀与防护学报, 2019, 39(2): 167-175.
[12] 达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[13] 赖德林,孔纲,车淳山. 硅酸盐封闭对TiO2转化膜耐蚀性的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 607-614.
[14] 邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[15] 邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.