富锌漆研究进展
谢德明
浙江大学热能工程研究所
The Development of Zinc-Rich Paints
Deming Xie
浙江大学热能工程研究所
全文: PDF(284 KB)  
摘要: 综述了70年来富锌漆的研究与应用的若干进展,对富锌漆的分类、防蚀机理、耐久性、性能特点以及存在的问题和补救措施等,进行了比较全面的评价。简单介绍了用于富锌漆的锌粉的分类和性能特点,此外,还介绍了有关富锌涂层电化学研究的一些进展。
关键词 富锌漆腐蚀电化学阻抗谱锌粉底漆面漆    
Abstract:The progress on the study and application of zinc-rich paints(ZRP) in the recent 70years has been reviewed. The design principle of ZRP and the problems of ZRP as topcoat systems and primer of multi-coatpaint systems were introduced The performance of different kinds of ZRP was compared. A brief introduction of zinc powder in ZRP was presented. The electrochemical study on ZRP was also summarized.
Key wordszinc-rich paints    corrosion    electrochemical impedance spectroscopy    zinc powder    primer    topcoat
收稿日期: 2003-02-10     
ZTFLH:  TG174.461  
通讯作者: 谢德明     E-mail: battery@cmee.zju.edu.cn
Corresponding author: Deming Xie     E-mail: battery@cmee.zju.edu.cn

引用本文:

谢德明 . 富锌漆研究进展[J]. 中国腐蚀与防护学报, 2004, 24(5): 314-320 .
Deming Xie. The Development of Zinc-Rich Paints. J Chin Soc Corr Pro, 2004, 24(5): 314-320 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2004/V24/I5/314

[1]Hare,CliveH .Tri-pigmentzincprimersystems[J].PaintandCoatings,1982,April:48
[2]PeartJohn.Organicvs.inorganiczinc-richinthefield[J].J .Pro tectiveCoatings&Linings,1992,9(2):46-53
[3]Kline,HarlanH .Inorganiczinc-rich[J].J .ProtectiveCoatings&Linings,1996,13(11):19
[4]WangGuoping.Thedevelopmentoftheshippingcoatings[J].China’sCoatings,2001,1:41(汪国平.船舶涂料与涂装的发展方向[J].中国涂料,2001,1:41)
[5]FeliuS ,BastidasJM ,MorcilloM .Effectofthedi-ironphosphideconductiveextenderontheprotectivemechanismsofzinc-richcoatings[J].J .CoatingsTechnology,1991,63(794):67-72
[6]LeclerqM .Productionofzincandzinc-alloyeddustsbyfineatom ization[J].J.OilColorChem.Association,1987,10:19
[7]Hare,CliveH .Zinc-richprimersI:designprinciples[J].J.Protec tiveCoatings&Linings,1998,15(7):17-38
[8]Brevoort,GordonH .Inorganiczinc-richcoatingsandgalvanizing:acomparison[J].J.ProtectiveCoatings&Linings,1996,13(9):66-74
[9]FeliuS ,BarajasR ,BastidasJM ,etal.Mechanismofcathodicprotec tionofzinc-richpaintsbyelectrochemicalimpedancespectroscopy:II .barrierstage[J].J .CoatingsTechnology,1989,61(775):71-76.
[10]FeliuS ,BarajasR ,BastidasJM ,etal.Mechanismofcathodicpro tectionofzinc-richpaintsbyelectrochemicalimpedancespec troscopy.I.galvanicstage[J].J .CoatingsTechnology,1989,61(775):63-69.
[11]LindquistSA ,MeszarosL ,SvensonL .Aspectsofgalvanicactionofzincrichpaints[J].J .OilColorChem.Association,1985,1:10
[12]VomagnoltR ,VetereVF .Themechanismofanticorrosiveactionofzincethylsilicatepaints[J].J .OilColorChem.Association,1993,5:208
[13]MorcilloM ,BarajasR ,FeliuS ,etal.SEMstudyonthegalvanicprotectionofzinc-richpaints[J].J.MaterialsScience,1990,25(5):2441-2446
[14]FeliuSebastianJr,BarajasRosa,BastidasJoseM ,etal.Studyofprotectionmechanismsofzinc-rich paintsbyelectrochemicalimpedancespectroscopy[A].ASTMSpecialTechnicalPublication[C].Philadelphia,PA ,USA ,PublishedbyASTM ,1993,1188:438-449
[15]UhligHH ,RevieRW .Anintroductiontocorrosionscienceandengineering[A].CorrosionandCorrosionControl,3 rded[C].JohnWiley,Sonsed.NewYork,1985:227
[16]BastidasJM ,FeliuSJr,MorcilloM ,etal.Studyoftheelectro chemicalnoisegeneratedbythemildsteel/zinc-richpaint/NaClsolutionsystem[J].ProgressinOrganicCoatings,1990,18(3):265-273
[17]RealSG ,EliasAC ,VilcheJR ,etal.Electrochemicalimpedancespectroscopystudyofzincrichpaintsonsteelsinartificialseawaterbyatransmissionlinemodel[J].ElectrochimicaActa,1993,38(14):2051-2054
[18]PereiraD ,ScantleburyJD ,FerreiraMGS ,etal.Applicationofelectrochemicalmeasurementstothestudyandbehaviorofzinc-richcoatings[J].Corros.Sci.,1990,30(11):1135-1147
[19]AlmeidaE ,PereiraD ,CabralAM ,etal.Anewapproachtothee valuationofazinc-richpolystyreneprimers[J].J .OilColorChem.Association,1991:21
[20]FaidiSE ,ScantleburyJD ,BullivantP ,etal.Electrochemicalstudyofzinc-containingepoxycoatingsonmildsteel[J].Corros.Sci.,1993,35(5-8,pt2):1319-1328
[21]FeliuS ,BarajasJM ,Morcillo,etal.Deteriorationofcathodicpro tectionactionofzinc-richpaintcoatingsinatmosphericexposure[J].Corrosion,2001,57(7):591-597
[22]FrydrychPJ .EISofzinc-richorganiccoatingsonsteel[J].Proct.Electrochem.Soc.,1987:240
[23]NovoaXR ,IzquierdoM ,MerinoP ,etal.Electrochemicalimpedancespectroscopyandzeroresistanceammeters(ZRA)astoolsforstudyingthebehaviorofzinc-richinorganiccoatings[J].Mater.Sci.Forum.,1989,44-45:223
[24]GervasiCA ,DiSarliAR ,CavalcantiE ,etal.Corrosionprotectionofsteelinseawaterusingzinc-richalkydpaints.Anassessmentofthepigment-contenteffectbyEIS [J].Corros.Sci.,1994,36(12):1963-1972
[25]IzquierdoM ,NovoaXR ,PenaG ,etal.Themechanismofprotec tionofzinc-richinorganiccoatings.Astudybasedonelectrochem icalimpedancespectroscopy(EIS)[J].Mater.Sci.Forum.,1992,111-112:257
[26]ZhangJQ .OnEISdisplaysofzinc-richcoatings[J].J.Chin.Soc.Corros.Prot.,1996,16:175-180.(张鉴清.富锌涂层的电化学阻抗谱特性[J].中国腐蚀与防护学报,1996:16(1):175-180)
[27]AbreuCM ,IzquierdoM ,KeddamM ,etal.Electrochemicalbehav iorofzinc-richepoxy paintsin3%NaClsolution[J].Elec trochim.Acta,1996,41(15):2405-2415
[28]AbreuCM ,EspadaL ,IzquierdoM ,etal.Factorsaffectingtheelectrochemicalbehaviorofzinc-richepoxypaints[J].EuropeanFederationCorrosionPublication,1997,20:23-32
[29]FeliuSJr,MorcilloM ,BastidasJM ,etal.Zincreactivityinzinc-richcoatingsco-pigmentedwithdi-ironphosphide[J].J.Coat ingsTechnology,1991,63(793):31-34
[30]KendigMK ,JeanjaquetSL ,WhiteJ,etal.Corrosionprotectionbyorganiccoatings[J].TheElectrochemicalSociety,1987,(87-2):253
[31]AbreuCM ,IzquierdoM ,MerinoP ,etal.Anewapproachtothedeterminationofthecathodicprotectionperiodinzinc-richpaints[J].Corrosion,1999,55(12):1173-1181
[32]DiSarliAR ,CavalcantiE ,FerrazO .UseofEIStocharacterizetheperformanceofnavalsteel/organiccoatingsystemsinNaClsolution[J].CorrosionPrevention&Control,1993,40(3):66-70
[33]CavalcantiE ,FerrazO ,DiSarliAR .Useofelectrochemicalimpedancemeasurementstoassesstheperformanceoforganiccoatingsystemsonnavalsteel[J].ProgressinOrganicCoatings,1993,23(2):185-200
[34]GervasiC ,ArmasR ,DiSarliAR ,etal.CorrosionmonitoringofZRPonsteelbyEIStoevaluatetheperformanceofdifferentcoat ingformulations[J].MaterialsScienceForum,1995,192-194(1):357-362
[35]MontesErnesto.Influenceofparticlesizedistributionofzincdustinwater-based,inorganic,zinc-richcoatings[J].J .CoatingsTechnology,1993,65(821):79-82
[36]ArmasRA ,GervasiCA ,DiSarliA ,etal.Zinc-richpaintsonsteelsinartificialseawaterbyelectrochemicalimpedancespec troscopy[J].Corrosion,1992,48(5):379-383
[37]YuZN .Anti-CorrosionCoatings&Painting[M].Beijing:Chem istryIndustryPress,1994:82(虞兆年.防腐蚀涂料与涂装[M ].北京:化学工业出版社,1994:82)
[38]FragataFL ,MussoiCRS ,MoulinCF ,etal.Influenceofextenderpigmentsontheperformanceofethylsilicatezinc-richpaints[J].J.CoatingsTechnology,1993,65(816):103-109
[39]RudolfA ,KaiserWolf-Dieter,FunkeWerner.Surface-modifiedzincdustpigmentsinanti-corrosioncoatings[J].Farbe&Lack,1994,100(12):1003-1005
[40]WangG ,LiXL ,LiangHW ,etal.Studyofmoisturecureurethanemodifiedbysiloxanescoupleanditsapplicationinzinc-richprimer[J].Mater.Prot,1997,30(8):3-4(王刚,李秀玲,梁鸿文等.硅烷偶联剂对湿固化聚氨酯的改性及在锌粉底漆中的作用[J].材料保护,1997,30(8):3-4)
[41]HareCliveH .Troublewithzinc-richprimers,PartI:Non-top coatedsystems[J].J .ProtectiveCoatings&Linings,1998,15(8):41
[42]ZhuH .Analysisofzincpowderinzinc-richprimer[J].TuliaoGongye,1998,28(2):38-42(朱洪.富锌底漆中锌粉的分析研究[J].涂料工业,1998,28(2):38-42)
[43]JinXH ,ZhengTS .Thestudyonlamellarzinc-richprimer[J].Mater.Prot.,1999,32(4):25-26(金晓鸿,郑添水.鳞片状锌基环氧富锌底漆的研究[J].材料保护,1999,32(4):25-26)
[44]WeldonDwightG ,CarlBruceM .Determinationofmetalliczinccontentofinorganicandorganiczinc-richprimersbydifferentialscanningcalorimetry[J].J.CoatingsTechnology,1997,69(868):45-49
[45]HareCliveH ,WrightSJ .Anticorrosiveprimersbasedonzincflake[J].J.CoatingsTechnology,1982,61(775):65
[46]GiudiceCBenftez,LinaresMM .Zinc-richepoxybasedonlamel larzincdust[J].SurfaceCoatingsInternational,1997(6):279-284
[47]HareCliveH .Troublewithzinc-richprimersII :Multi-coatpaintsystems[J].J.ProtectiveCoatings&Linings,1998,15(9):38-46
[48]KweonYG ,CoddetC .Behaviorinseawaterofzinc-basecoatingsonaluminumalloy5086[J].Corrosion,1992,48(2):97-102
[49]VlietCHvan.Reductionofzincandvolatileorganicsolventsintwo-packanti-corrosiveprimers-apilotstudy[J].ProgressinOr ganicCoatings,1998,34:220-226
[1] 董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2] 唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3] 韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4] 张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9] 郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10] 于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11] 贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12] 赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13] 马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14] 岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15] 艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.