稀土铒和铬离子注入对电机护环钢SCC性能的影响
靳九成;谢中;吴翠兰;李建明;靳诰;钟庆东;王培大;龙奔;刘国宾
湖南大学;中国科学院半导体研究所;东方电机厂
EFFECTS OF ION IMPLANTATION WITH RARE-EARTH ERBIUM AND CHROMIUM ON SCC BEHAVIOUR FOR GENERATOR RETAINING RING STEEL
Jin Jiucheng; Xie Zhong; Wu Cuilan; Li Jianming; Jin Hao; Zhong Qingdong (Hunan University)Wang Peida(Institute of Semiconductor;Chinese Academy Of Sciences)Long Ben; Liu Guobin(Dongfang Electrical Machinery Works)
全文: PDF(1412 KB)  
摘要: 研究了解和铬离子高、中能量重迭注入对50Mn18Cr4电机护环钢SCC性能的影响.SCC对比试验结果表明:(1)在QHJ-79标准硝酸盐介质中,离子注入试样的SCC出现时间(tf)比不经注入试样的延长了6倍以上,致钝和维钝电流密度下降了一个数量级;(2)在阴极充氢条件下,两种试样均对氢致开裂(HIC)不敏感,但离子注入可抑制氢诱发腐蚀.用AES-PRO、RBS、XPS-PRO、EDAX、金相及电化学方法分析讨论了护环钢在QHJ-79标准介质中的SCC机理和离子注入改善SCC抗力及抗氢锈发腐蚀性能的机制.
关键词 电机护环钢Er~++Cr~+注入SCC    
Abstract:The effeCts of overlap-implanting rare-earth erbium and chromuim ions with high-medium energy on stress corrosion cracking (SCC) have been studied for generator retaining ring steel 50Mn18Cr4. The results of comparstive SCC tests show that: (1) The time to SCC appearance if in the nitrate solution prepared according to QHJ-79 standard for implanted specimens is postponed averagely over 6 times, and the critical current densities required to cause and maintain passivation decrease by one order of magnitude. (2) In the medium for cathodally charging of hydrogen, the steel is insensitive to hydrogeninduced corrosion (HIC); the HIC resistance can be improved by Er++Cr+ implantation remarkably. The mechanism of SCC for the steel in QHJ-79 standard solution and of improvement of resistance to SCC and HIC by ion-implantation is discussed on the basis of the results of AES-PRO, RBS, XPS-PRO, EDAX, metallography and electrochemistry tests.
Key words generator retaining ring steel    rare-earth    erbium    chromium    ion-implantation    SCC
收稿日期: 1994-06-25     
基金资助:中国科学院上海冶金研究所离子束开放研究实验室资助;;中国科学院腐蚀科学开放研究实验室基金

引用本文:

靳九成;谢中;吴翠兰;李建明;靳诰;钟庆东;王培大;龙奔;刘国宾. 稀土铒和铬离子注入对电机护环钢SCC性能的影响[J]. 中国腐蚀与防护学报, 1994, 14(3): 231-239.
. EFFECTS OF ION IMPLANTATION WITH RARE-EARTH ERBIUM AND CHROMIUM ON SCC BEHAVIOUR FOR GENERATOR RETAINING RING STEEL. J Chin Soc Corr Pro, 1994, 14(3): 231-239.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y1994/V14/I3/231

1KatsutoshiORITA.YasumiIKEDA;TadaoIWADATEandJunjiISHIZAKA.ISIJInternational,1990,3O(8):5872于福洲编著,金属材料的耐腐蚀性,北京:科学出版社,19823诸武扬著.氢损伤和滞后断裂,北京:冶金工业出版社,19884靳九成,赵传国等编著.磨削变质层及表面改性,长沙:湖南大学出版社,1988
[1] 刘智勇; 李明; 李晓刚 . 16Mn(HIC)钢在硫化氢环境中的应力腐蚀开裂行为[J]. 中国腐蚀与防护学报, 2006, 26(6): 360-365 .
[2] 唐建群; 巩建鸣; 涂善东 . 不同钢制造LPG球罐在湿H2S环境下失效行为的对比研究[J]. 中国腐蚀与防护学报, 2006, 26(4): 245-250 .
[3] 张亦良; 王晶; 陕小平; 李邦宪 . CNG气瓶在不同H2S浓度中的临界裂纹尺寸[J]. 中国腐蚀与防护学报, 2005, 25(5): 285-290 .
[4] 高红霞 . 渗铝304不锈钢不同实验方法的SCC敏感性评价[J]. 中国腐蚀与防护学报, 2004, 24(5): 289-292 .
[5] 许淳淳;欧阳维真;徐瑞芬;吴永炘. 1Cr18Ni9Ti不锈钢在氯化物溶液中SCC敏感性与铁磁相含量的相关性[J]. 中国腐蚀与防护学报, 1997, 17(1): 73-76.
[6] 蒋兴钢;褚武扬;肖纪美. 应力腐蚀门槛值和断口分形维的定量关系[J]. 中国腐蚀与防护学报, 1995, 15(1): 57-60.