Fe-26Cr-1Mo不锈钢在腐蚀疲劳过程中的瞬态电流行为

中国腐蚀与防护学报

1992, Vol. 12

Issue (4): 358-364

研究报告

本期目录 | 过刊浏览

Fe-26Cr-1Mo不锈钢在腐蚀疲劳过程中的瞬态电流行为

颜晓明;马敏雅;朱自勇;王中光

中国科学院金属研究所;中国科学院金属研究所;中国科学院金属腐蚀与防护研究所;中国科学院金属研究所

THE CURRENT TRANSIENT BEHAVIOUR OF Fe-26Cr-1Mo STAINLESS STEEL DURING CORROSION FATIGUE

Yan Xiaoming~*; Ma Minya~*; Zhu Ziyong~(**) and Wang Zhongguang~* *(Institute of Metal Research; Chinese Academy of Sciences) **(Institute; of Corrosion and Protection of Metals; Chinese; Academy of Sciences)

全文: PDF(506 KB)

摘要: <正>一、引言在腐蚀性水溶液中,金属的力学疲劳损伤因电化学作用(如溶解效应和氢还原反应等)而加剧,反之,在腐蚀疲劳过程中,力学疲劳引起的塑性形变局部化又会增加电化学腐蚀。

Abstract：Push-pull fatigue tests under plastic strain control were carried out with a high-purity ferritic stainless steel Fe-26Cr-1Mo in 1mol/L H_2SO_4 and 1mol/L NaCl solutions. The current transient behaviour during corrosion fatigue was different in these two solutions. Two sharp current peaks corresponding to maximum tensile and compressive strains respectively were observed in 1mol/L H_2SO_4. A sudden current drop or bump occurred as the test started with tension in H_2SO_4 solution. However, only one current peak, which occurred at approximately 50％ of the applied tensile strain, was found in each strain period in NaCl solution. The experimental results were explained in terms of the depassivation-repassivation process induced by strain cycling with the effect of chloride ions taken into account.

收稿日期: 1992-08-25

基金资助:国家自然科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	颜晓明
	马敏雅
	朱自勇
	王中光
44.8K

引用本文:

颜晓明;马敏雅;朱自勇;王中光. Fe-26Cr-1Mo不锈钢在腐蚀疲劳过程中的瞬态电流行为[J]. 中国腐蚀与防护学报, 1992, 12(4): 358-364.
. THE CURRENT TRANSIENT BEHAVIOUR OF Fe-26Cr-1Mo STAINLESS STEEL DURING CORROSION FATIGUE. J Chin Soc Corr Pro, 1992, 12(4): 358-364.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1992/V12/I4/358

[1] Pyle,T.Rollins,V.and Howard,D.J.Electrochem.Soc.,122． 1445(1975)
[2] ortner,S.and Laird,C.Acta Metall.,35,867(1987)
[3] Magnin,T.aNd Coudreuse,L.Mater.Sci.Eng.,72,125(1985)
[4] Magnin,T.and Coudreuse,L.Acta Metall.,35,2105(1987)
[5] 王中光,柯伟,材料科学和工程,No.3,P26,(1983)
[6] Choo,Y.H.and Deverex,O.F.J.Electrochem.Soc.,123,1863(1976)
[7] Ortner,S.Ph.D.Dissertation,the University of Pennsylvania,USA 1985
[8] Li,Y.F.Private Communication,the University of Pennsylvania,USA 1989
[9] Sato,N.and Okamoto,G.Comprehensive treatises of Electrochem.,4,Edited by Bockris etc.,plenam Publishing Cor.poration,1981

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed