表面有Na_2SO_4沉积时铁基合金的低温热腐蚀行为

张允书;史良权;石声泰

中国科学院上海冶金研究所;中国科学院上海冶金研究所;中国科学院上海冶金研究所

LOW TEMPERATURE HOT CORROSION BEHAVIOR OF IRON BASE ALLOYS IN THE PRESENCE OF Na_2SO_4 DEPOSIT

Zhang Yunshu; Shi Liangquan and Shih Shengtai (Shangghai Institute of Metallurgy; Chinese Academy of Sciences)

全文: PDF(1614 KB)

摘要: 研究了工业纯铁、Fe-Cr和Fe-Al合金表面有Na_2SO_4沉积时于O_2/SO_2/SO_3气氛中的低温热腐蚀行为。测定腐蚀动力学曲线,研究温度、气体组成及合金元素对腐蚀动力学的影响,并对腐蚀产物的形貌和组成进行观察与分析。结果表明,在工业纯铁、Fe-Cr和Fe-Al合金的低温热腐蚀过程中都发生金属表面致密氧化层的快速成长和疏松的Fe_2O_3在盐膜中的沉积,且前者对腐蚀的贡献居大。以实验结果为依据,初步提出了电化学机理模型,并用以阐述铁基合金低温热腐蚀过程。

Abstract：Hot corrosion behavior of commercial iron and Fe-Cr,Fe-Al alloys in the presence of a thin Iayer of Na_2SO_4 deposit was studied in O_2/SO_2/SO_3 gas atmospheres at 650～750℃. The reaction kinetics were monitored and found to be dependent upon temperature, gas composition and alloy element content. XRD, SEM, EPMA and chemical analysis were employed to characterize the corrosion products. The results showed that the corrosion product scale for each material tested was composed of a compact oxide plus sulfide layer and a porous Fe_2O_3 plus salt layet. The both layers increased in thickness with the proceeding of corrosion, and the compact layer grew faster than the porous one. On the basis of experimental results, an electrochemical mechanism is preliminarily proposed, and it is used to illustrate low temperature hot corrosion processes of iron base alloys.

收稿日期: 1992-06-25

基金资助:中国科学院腐蚀科学开放研究实验室课题;;国家基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张允书
	史良权
	石声泰
44.8K

引用本文:

张允书;史良权;石声泰. 表面有Na_2SO_4沉积时铁基合金的低温热腐蚀行为[J]. 中国腐蚀与防护学报, 1992, 12(3): 5-195.
. LOW TEMPERATURE HOT CORROSION BEHAVIOR OF IRON BASE ALLOYS IN THE PRESENCE OF Na_2SO_4 DEPOSIT. J Chin Soc Corr Pro, 1992, 12(3): 5-195.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1992/V12/I3/5

[1] Reid, W.T. ; Corey, R.C. and Cross. B. J. Trans. ASME, 67, 279(1945)
[2] NeLson, W. and Cain Jr, C, Trans. Am. Mech. Engrs. J. Eng'g Pr. 82A, 194(1960)
[3] Cortier, J. ,in "Mechanism of Corrosion by Fuel Impurities",Janson, M.R. and Litter, D. J.. Eds., Butterworths, London, P. 531, (1963)
[4] 张允书、李选明、石声泰,中国腐蚀与防护学报,10,1(1990)
[5] 张允书、李选明、史良权、石声泰,中国腐蚀与防护学报,11,17(1991)
[6] 史良权、张允书、石声泰,中国腐蚀与防护学报,10,135(1990)
[7] 张允书、史良权、石声泰,中国腐蚀与防护学报,12(1) ,20(1992)
[8] 史良权,中国科学院上海治金研究所博士论文,(1990)
[9] 张允书、李选明、曹铁梁、石声泰,腐蚀科学与防护技术,4(1) ,9(1992)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed