超高强度钢应力腐蚀断口的分形维数研究

中国腐蚀与防护学报

1991, Vol. 11

Issue (4): 344-352

研究报告

本期目录 | 过刊浏览

超高强度钢应力腐蚀断口的分形维数研究

陈军;龙起易;陈继志;龙期威

中国科学院全属研究所;中国科学院全属研究所;中科院国际材料物理中心;中国科学院全属研究所;中国科学院全属研究所;中科院国际材料物理中心

A STTDY OF FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS CORROSION CRACKING IN HIGH STRENGTH STEEL

Chen Jun Long Qiyi Chen Jizhi Long Qiwei 1. (Institute of Metal Research; Academia Sinica) 2. (International Centre For Materials Physics; Academia Sinica)

全文: PDF(1788 KB)

摘要: 用垂直剖面法测定了30CrMnSiNi2钢在去离子水中应力腐蚀开裂断口的分形维数。结果表明,在裂纹扩展过程中裂纹尖端塑性区保持很小的条件下,应力腐蚀开裂形成的断裂表面的分形维数与断面的有效表面能密度γ_p之间有正的变化关系。在本工作试验条件下,应力腐蚀开裂过程是使断裂表面增维的过程。文中分析了失稳扩展区断裂表面的分维比紧邻的亚稳扩展区表面的分维低的原因。

Abstract：Fractal dimension of different parts of two fracture surfaces created by stress corrosion cracking in a high strength steel has been investigated by means of fracture profile analysis. The results show that the fractal dimension of the fracture surface corresponding to the sub-critical propagtion zone increases as the crack propagates. Therefore the process of stress corrosion cracking is the one during which the fractal dimension of the fracture surface increases.

收稿日期: 1991-08-25

基金资助:国家自然科学基金

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈军
	龙起易
	陈继志
	龙期威
44.8K

引用本文:

陈军;龙起易;陈继志;龙期威. 超高强度钢应力腐蚀断口的分形维数研究[J]. 中国腐蚀与防护学报, 1991, 11(4): 344-352.
. A STTDY OF FRACTAL DIMENSION OF FRACTURE SURFACE CREATED BY STRESS CORROSION CRACKING IN HIGH STRENGTH STEEL. J Chin Soc Corr Pro, 1991, 11(4): 344-352.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1991/V11/I4/344

[1] Mandelbrot. B. B., Fractals: Form Chance and Dimension, Freeman, San Francisco CA , 1977,32
[2] Mandelbort. B. B., Passoja. D. E., and Paullay A. J., Nature, 308, 721(1984)
[3] Pande. C. S., Richards. L. E., Louat. N., Dempsey. B. D, and Schwoeble. A. J., Acta Metall. 35 1633 1987
[4] 穆在勤,龙期威,金属学报,24(2) ,P142,(1988)
[5] Dauskardt. R. H., tiaubensak. F., and Ritchipe. R. O., Acta Metappll. Mater. 38(2) , 143(1990)
[6] Underwood. E. E, and Banerji. K.; Mater Sci Eng., 80, 1(1986)
[7] Brown. B.F. Beachem. C.D., Corros. Sci., 5, 745(1965)
[8] Mandelbrot. B. B., The Fractal Geometry of Nature, Freemam San Francisco (1983)
[9] Tetelman A. S., Fracture of Solids, Edited by Dtucker. D.C. and Gilman. J.J., Interscience Publishers, P461,(1962)
[10] Gilman. J.J., J. Appl. Phys. 27, 1262 (1956)
[11] Mott. N. F., Engineering, 16, 165(1848)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed