渗铝对CoCrAlY溅射涂层抗热腐蚀性能的影响

楼翰一;王福会;白林祥

中国科学院金属腐蚀与防护研究所;中国科学院金属腐蚀与防护研究所;中国科学院金属腐蚀与防护研究所

EFFECT OF ALUMINIZING ON THE HOT CORROSION RESISTANCE OF THE SPUTTERED CoCrAlY COATING

Lou Hanyi Wang Fuhui Bai Linxiang (Institute of Corrosion and Protection of Metals; Academia Sinica)

全文: PDF(3117 KB)

摘要: <正> 一、前言 MCrAlY涂层具有优良的抗热腐蚀性能,适用于运行参数高、使用环境恶劣的燃气轮机涡轮叶片。用离子溅射工艺制备的MCrAlY涂层,具有成份容易控制,组织比较致密的优点,因而越来越受到重视。此工艺需用与涂层同成份合金制成的靶,但由于机械加工的原因,常选用高铬低铝型靶材。这种类型的MCrAlY涂层在熔融硫酸盐环境中具有良好的抗热腐蚀性,但在含氯化钠的熔盐环境中抗蚀性变差,热腐蚀孕育期缩短。采用渗铝可提高MCrAlY涂层中

Abstract：The hot corrosion behaviour of Co-30Cr-6Al-0. 5Y coating produced by magnetron sputtering deposition and that of the said coating with subsequent aluminizing have been investigated in sulphate melt,but its hot corrosion resistance in molten salts. The results show that the CoCrAlY coating possesses excellent hot corrosion resistance in sulphate melt,but its hot corrosion resistance in molten salts containing NaCl is reduced severely after 100 hrs. With subsequent aluminizing of the CoCrAlY coating its resistance to hot corrosion is only slightly reduced in sulphates melt and is remarkably improved in salt melt containing NaCl. The different influence factors of aluminizing on the hot corrosion resistance of the CoCrAlY coatings in various salt melts have been discussed.

收稿日期: 1991-04-25

基金资助:中国科学院腐蚀科学开放研究实验室课题

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	楼翰一
	王福会
	白林祥
44.8K

引用本文:

楼翰一;王福会;白林祥. 渗铝对CoCrAlY溅射涂层抗热腐蚀性能的影响[J]. 中国腐蚀与防护学报, 1991, 11(2): 181-187.
. EFFECT OF ALUMINIZING ON THE HOT CORROSION RESISTANCE OF THE SPUTTERED CoCrAlY COATING. J Chin Soc Corr Pro, 1991, 11(2): 181-187.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1991/V11/I2/181

[1] Goward, G.W. Mater. Sci. Tcehnol.,2,194(1986)
[2] Rickerby, D. S. and Wood,W.I.,J. Vac. Sci. Technoi., A4,2557(1988)
[3] MeKee, D. W., Shores, D. A., and Luthra. K. L., J. Electrochem. Soc.,125,4119(1978)
[4] 楼翰一,王福会.嵇立润,张立新,金属学报,25,B380(1989)
[5] Batocci, R.S., Hot Corrosion Problems Associated with Gas Turbines, ASTM STP 421, 169(1967)
[6] Godlewski, K. and Godlewska,E., Mater. Sci. Eng.,88,103(1987)
[7] Lou, H. Y., Wang, F. H. and Bai, L.X., Mater. Sci. Eng.,A123(1) , 123(1990)
[8] Smeggil, J.G., Mater. Sci. Eng.,87,261(1987)
[9] 楼翰一,白林祥.王福会,王石军,中国腐蚀与防护学报,9,95(1989)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed