15Mn钢在3.5%氯化钠水溶液中的腐蚀疲劳

邢志强;宋余九

西安交通大学;西安交通大学

FATIGUE CRACK GROWTH OF 15Mn STEEL IN 3.5％ NaCl SOLUTION

Xing Zhiqiang Song Yujiu (Xi'an Jiaotong University)

全文: PDF(2390 KB)

摘要: 研究了不同组织状态的15Mn钢在3.5％氯化钠水溶液中的疲劳裂纹扩展行为,测定了裂尖区的平均氢含量和裂纹闭合力,发现外部条件(力学及环境)和材料的显微组织对腐蚀疲劳有重要影响。结合断口和裂纹走向观察,提出了15Mn钢腐蚀疲劳断裂的复合机制和断裂机制图。

Abstract：The crack growth of 15Mn steel with various microstructures in 3.5％ NaCl solution was investigated, It is found that the microstructures of steels have Considerable influence on corrosion fatigue. With increasing Stress intensities,crack closure effect decreases and average hydrogen content at crack tip increases. The fracture modes vary from striations to intergranular fracture and then to quasi-cleavage fracture with crack growth. The relation between electrochemical conditions and mechanical variables is discussed. The componund mechanisms of corrosion fatigue are proposed. A fracture-mode-map of 15Mn steel is worked out.

收稿日期: 1989-06-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	邢志强
	宋余九
44.8K

引用本文:

邢志强;宋余九. 15Mn钢在3.5%氯化钠水溶液中的腐蚀疲劳[J]. 中国腐蚀与防护学报, 1989, 9(3): 184-191.
. FATIGUE CRACK GROWTH OF 15Mn STEEL IN 3.5％ NaCl SOLUTION. J Chin Soc Corr Pro, 1989, 9(3): 184-191.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1989/V9/I3/184

[1] 邢志强、黄淑菊、宋余九、涂铭旌,第五届全国断裂学术会议论文集,596(1988)
[2] Guo Zhenfeng, ICM 5, Yan, M,Go and Zhang S. H. eds., Beijing, 1978, Pergaman press, 521
[3] Kichiro Endo, ASTM STP 801, 81
[4] Brown, B. F., The Theory of Stress Corrosion Cracking in Alloys, Seully ed., England, University of Leeds, 198(1971)
[5] Panasyuk, V. V., et al, Fatigue Eng. Mater. Struet., 7, 1(1984)
[6] 邢志强,西安交通大学硕士论文,(1985)
[7] Nebe, K., J. Appl. Phys., 29, 1632(1958)
[8] Giddings, J. C., et al, J. Electrochem. Soc. 106, 91(1959)
[9] Bristoll, P., European Offshore Steels Research Seminar, Cambridge, 1978, V/P18
[10] Turnbull, A., J. Electrochem. Soc., 129, 1412(1982)
[11] 林栋梁,吴建生、杨正瑞,金属学报,19(3) ,A 165(1983)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed