用研究均匀腐蚀的方法探讨不锈钢孔蚀的稳定发展

魏宝明;郝凌;杨忠英

南京化工学院;南京化工学院;南京化工学院

AN APPROACH TO THE PITTING STEADY GROWTH OF 18-8 AUSTENITIC STAINLESS STEEL UNDER UNIFORM CORROSION CONDITION

Wei Baoming Hao Ling Yang Zhongying (Nanjing Institute of Chemical Technology)

全文: PDF(641 KB)

摘要: 通过研究18-8奥氏体不锈钢在模拟孔内溶液中的均匀腐蚀行为,定量研究了孔内溶液浓度和温度对孔蚀发展速率的影响。测定了试样在模拟孔内溶液中的极化曲线,并将极化曲线的塔菲尔区直线外推,得到理想极化曲线和自腐蚀电流密度,据此对测定实际孔蚀速率的间接方法作了初步探讨,并对孔蚀核再钝化的条件作了详细讨论。

Abstract：The effect of the solution temperature and concentration within pits on pitting growth rate of 18-8 austenitic stainless steel has been studied quantitatively under uniform corrosion condition. The practical polarzation curves (PPC) of the sample was measured in the simulated solutions within the pits. The ideal polarization curves and corrosion current densities were obtained by extrapolating the Tafe's lines of the PPC to corrosion potentials. The requirements for repassivation of pitting nuclei were discussed in detail. According to the experimental results, the authors attempted an initial approach to a method for measuring the practical rate of pitting growth.

收稿日期: 1988-04-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	魏宝明
	郝凌
	杨忠英
44.8K

引用本文:

魏宝明;郝凌;杨忠英. 用研究均匀腐蚀的方法探讨不锈钢孔蚀的稳定发展[J]. 中国腐蚀与防护学报, 1988, 8(2): 113-119.
. AN APPROACH TO THE PITTING STEADY GROWTH OF 18-8 AUSTENITIC STAINLESS STEEL UNDER UNIFORM CORROSION CONDITION. J Chin Soc Corr Pro, 1988, 8(2): 113-119.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1988/V8/I2/113

[1] et al., Z. Phys. Chem., 226, 25(1964)
[2] Engell, H. J., et al., Z. Phys. Chem., 20, 113(1959)
[3] Stolica, Z. D., Corros. Sci,, 9, 455(1969)
[4] Oldfield, J. W.; Sutton, W. H., Brit. Corros. J., 13, 107(1978)
[5] 腐蚀与耐腐蚀合金,曹铁梁等译,化学工业出版社,P.62 (1982)
[6] Tsuguo Suzuki, et al., Corrosion, 29, 18(1973)
[7] Sandoz, G.; Fujii, C. T.; Brown, B. F., Corros. Sci., 10, 839(1970)
[8] Lekie, H. P., J. Electrochem. Soc., 113, 1262(1966)
[9] 魏宝明等,南京化工学院学报,8(2) ,33(1986)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed