电化学方法研究12Cr2MoAlXt钢在海水中的耐蚀性
黄亚敏;苏方腾
中国科学院福建物质结构研究所;中国科学院福建物质结构研究所
AN ELECTROCHEMICAL STUDY ON THE CORROSION RESISTANCE OF 12Cr_2MoAlXt ALLOY STEEL IN SEA WATER
Huang Yamin Su Fangteng (Fujian Institute of Research on the Structure of Matter;Academia Sinica)
全文: PDF(393 KB)  
摘要: <正> 一、前言12Cr2MoAlXt 低合金钢是一种新钢种,具有良好的耐海水腐蚀性能。为了探讨该钢种的耐蚀原因以及比较测试腐蚀速度的几种常用方法,我们测定了12Cr2MoAlXt 钢和 A3钢在海水中的电化学性质。
Abstract:Electrochemical potentiodynami cpolarization,linear polarization and weight loss methods,were used to study the corrosion behavior of 12Cr2MoAlXt steel in sea water. Experimental results showed that the limiting oxygen diffusion current on 12Cr2MoA1Xt steel was much smaller than that on A3 steel and reached a steady value in a few days.It was supposed to be the main factor for improved corrosion resistance in sea water.
收稿日期: 1988-02-25     

引用本文:

黄亚敏;苏方腾. 电化学方法研究12Cr2MoAlXt钢在海水中的耐蚀性[J]. 中国腐蚀与防护学报, 1988, 8(1): 72-77.
. AN ELECTROCHEMICAL STUDY ON THE CORROSION RESISTANCE OF 12Cr_2MoAlXt ALLOY STEEL IN SEA WATER. J Chin Soc Corr Pro, 1988, 8(1): 72-77.

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y1988/V8/I1/72

[1] 青岛海洋用钢试验站,海洋用低合金钢统一评定试验第二周期总结,(1981)
[2] 南京化工学院防腐蚀教研室,兰州化机所四室和北京化工学院防腐蚀教研室,北京化工防腐蚀(钢材耐蚀性能快速测定)专辑(1976)
[3] 苏方腾.中国腐蚀与防护学报,1(1) ,25(1981)
[4] 马中华,崔秀岭,中国腐蚀与防护学报,1(1) ,19(1981)
[5] 马如章,吴继勋,中国腐蚀与防护学报,1(3) ,48(1981)
[6] Chen,J.M.(陈俊明)et al.,Prcceeding of 9th Internationol Congress on Metallic Corrosion,1984,Toronto,4,5~9 5~9(1984)
[7] Wranglen,G.,Corrosion Science,14(5) ,311(1974)
[8] 上海钢铁研究所主编,国外海洋用金属材料,239
[9] 吴荫顺,杨德钓,吴继勋,中国腐蚀与防护学报,1(2) ,14(1981)
No related articles found!