析出相对Cr-Mn-N奥氏体不锈钢应力腐蚀性能的影响

姚治铭;李有柯;王守芬;赵一省;乔蕴兰

中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所;中国科学院金属研究所

THE EFFECT OF PRECIPITATES ON THE STRESS CORROSION CRACKING BEHAVIOR OF Cr-Mn-N AUSTENITIC STAINLESS STEEL

Yao Zhimin Li Youko Wang Shoufen Zhao Yishen Qiao Funlan(Institute of Metal Research; Academia Sinica; Shenyang)

全文: PDF(1950 KB)

摘要: 本文研究了合金碳化物M_(23)C_6和金属间化合物x相对Cr-Mn-N奥氏体不锈钢应力腐蚀性能的影响。结果指出,在4NNaCl溶液中,上述两种沉淀相对钢的自然腐蚀电位和不同电位下的断裂时间影响明显,而在45％MgCl_2溶液中,两种沉淀相的影响甚微。从断裂机制上对两种沉淀相的影响进行了讨论。

Abstract：The effect of M_(23)C_6 and intermetallic compound x-phase on the stress corrosion cracking behavior of a Cr-Mn-N austenitic stainless steel was studied in 4N NaCl and 45％ MgCl_2 solutions. The results showed that the two precipitates had a pronounced influence on open circuit potential and the time to failure at various applied potentials in 4N NaCl solution while they had little effect in the 45％ MgCl_2 solution. The different effects of these two precipitates in above mentioned solutions were related to different failure mechanisms.

收稿日期: 1983-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	姚治铭
	李有柯
	王守芬
	赵一省
	乔蕴兰
44.8K

引用本文:

姚治铭;李有柯;王守芬;赵一省;乔蕴兰. 析出相对Cr-Mn-N奥氏体不锈钢应力腐蚀性能的影响[J]. 中国腐蚀与防护学报, 1983, 3(4): 254-260.
. THE EFFECT OF PRECIPITATES ON THE STRESS CORROSION CRACKING BEHAVIOR OF Cr-Mn-N AUSTENITIC STAINLESS STEEL. J Chin Soc Corr Pro, 1983, 3(4): 254-260.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1983/V3/I4/254

[1] Steigerwald, R. F., Corrosion, 33, 338(1977)
[2] 《海洋用钢腐蚀研究》,上海钢铁研究所主编,上海科学技术出版社,27(1978)
[3] Mukherjee, G. K., Nijhawan, B. R., J. Iron and Steel Inst., 205, 62(1967)
[4] O'Dell, C. S, ef al. Corrosion, 36． 183(1980)
[5] Scheil, M. A., Symposium on Stress Corrosion Cracking of Metals, ASTMAIME, (1945)
[6] 村田稚人,向井喜彦,日本金属学会志,44,230(1980)
[7] Suzuki, T., Kitamura, Y., Corrosion, 28, 1(1972)
[8] Shamakian, R. L.; et al., ibid., 36, 279(1980)
[9] Mohr, T. W.; ef al., Corrosion, 37, 199(1981)

No related articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed