中国腐蚀与防护学报  2018, Vol. 38 Issue (6): 558-564    DOI: 10.11902/1005.4537.2017.203
  本期目录 | 过刊浏览 |
低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究
刘明1,2(),程学群3,李晓刚3,4,卢天健1,5
1. 西安交通大学航天航空学院 多功能材料与结构教育部重点实验室 西安 710049
2. 西安交通大学 机械结构强度与振动国家重点实验室 西安 710049
3. 北京科技大学 腐蚀与防护中心 北京 100083
4. 中国科学院宁波材料技术与工程研究所 宁波 315201
5. 南京航空航天大学 机械结构力学与控制国家重点实验室 南京 210016
Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract
Ming LIU1,2(),Xuequn CHENG3,Xiaogang LI3,4,Tianjian LU1,5
1. MOE Key Laboratory for Multifunctional Materials and Structures, Xi'an Jiaotong University, Xi'an 710049, China
2. State Key Laboratory for Strength and Vibration of Mechanical Structures, Xi'an Jiaotong University, Xi'an 710049, China
3. Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China
4. Ningbo Institute of Material Technology & Engineering, Chinese Academy of Sciences, Ningbo 315201, China
5. State Key Laboratory of Mechanics and Control of Mechanical Structures, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;orrespondent: LIU Ming, E-mail: liuming0313@xjtu. edu. cn
全文: PDF(3374 KB)   HTML
摘要: 

采用动电位极化曲线、Mott-Schottky结合XPS和AES,分析研究了Cr对耐蚀钢筋在水泥萃取液中形成的钝化膜的耐蚀机理。结果表明,随着浸泡时间的延长,钢筋电极的自腐蚀电流密度 (Icorr) 降低,浸泡1 d后可以形成具有保护性的钝化膜。Cr含量的增加减小了钢筋钝化膜中的载流子密度,提高了其稳定性。Cr含量的增加抑制了Fe2+向Fe3+的氧化过程,从而提高了钢筋钝化膜的耐蚀性。耐蚀钢筋中的Cr参与了钝化膜的形成,稳定钝化膜则主要由Fe的氧化物组成;钝化膜内层为含Cr-Fe的氧化物,外层为Fe的氧化物;钝化膜的厚度在3~4 nm之间,随Cr含量的增加而略微增大。

关键词 耐蚀钢筋钝化膜Mott-SchottkyX射线光电子能谱俄歇电子能谱    
Abstract

Influence of Cr content on the corrosion resistance of passive films formed on low alloyed rebar steels in liquor of cement extract was studied by means of electrochemical techniques, X-ray photoelectron spectrometer and auger electron spectroscopy. TheIcorrof steel electrodes is found to decrease with increasing immersion time, and protective passive films could form after 1 d immersion. The increase of Cr content decreases the carrier density of the passive films, thereby improves their stability. The increase of Cr content inhibits the oxidation process of Fe2+to Fe3+, thus enhance the corrosion resistance of the passive films. Stable passive films are primarily consisted of iron oxides with a thickness of 3~4 nm. As Cr is involved in the formation of passive films, which induces the formation of an inner layer of complex Cr-Fe oxides beneath the outer layer of Fe oxides. The film thickness slightly increases as the content of Cr increases.

Key wordscorrosion resistance steel rebar    passive film    Mott-Schottky    XPS    AES
收稿日期: 2017-11-28     
ZTFLH:  TG172  
基金资助:国家自然科学基金(51801149);中国博士后基金(2017M620448)
通讯作者: 刘明     E-mail: liuming0313@xjtu.edu.cn
Corresponding author: Ming LIU     E-mail: liuming0313@xjtu.edu.cn
作者简介: 刘明,男,1987年生,博士,助理研究员

引用本文:

刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
Ming LIU, Xuequn CHENG, Xiaogang LI, Tianjian LU. Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract. Journal of Chinese Society for Corrosion and protection, 2018, 38(6): 558-564.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2017.203      或      https://www.jcscp.org/CN/Y2018/V38/I6/558

图1  HRB400及其3种Cr合金化的钢筋在水泥萃取液中浸泡不同时间后的极化曲线
图2  4种钢筋电极在水泥萃取液中浸泡7 d后的Mott-Schottky曲线
图3  4种钢筋电极在水泥萃取液中浸泡7 d后表面Fe2p3/2的XPS谱
图4  钢筋电极在水泥萃取液中浸泡7 d后表面Cr2p3/2的XPS谱
图5  钢筋电极在水泥萃取液中浸泡7 d后表面O1s的XPS谱
图6  4种钢筋电极在水泥萃取液中浸泡7 d后Fe,Cr和O从表面沿深度分布的XPS分析结果
[1] Liu M,Cheng X Q,Li X G,et al.Effect of Cr on the passive film formation mechanism of steel rebar in saturated calcium hydroxide solution[J].Appl. Surf. Sci.,2016,389:1182
[2] Liu M,Cheng X Q,Li X G,et al.Effect of carbonization on the electrochemical behavior of corrosion resistance low alloy steel rebars in cement extract solution[J].Constr. Build. Mater.,2016,130:193
[3] Liu M,Cheng X Q,Zhao G C,et al.Corrosion resistances of passive films on low-Cr steel and carbon steel in simulated concrete pore solution[J].Surf. Interface Anal.,2016,48:981
[4] Hakiki N E.Comparative study of structural and semiconducting properties of passive films and thermally grown oxides on AISI 304 stainless steel[J].Corros. Sci.,2011,53:2688
[5] Freire L,Carmezim M J,Ferreira M G S,et al.The passive behaviour of AISI 316 in alkaline media and the effect of pH: A combined electrochemical and analytical study[J].Electrochim. Acta,2010,55:6174
[6] Mancio M,Kusinski G,Monteiro P J M,et al.Electrochemical andin-situSERS study of passive film characteristics and corrosion performance of 9%Cr microcomposite steel in highly alkaline environments[J]. J. ASTM Int.,2009,6:1
[7] Macdonald D D,Biaggio S R,Song H.Steady-state passive films: Interfacial kinetic effects and diagnostic criteria[J]. J. Electrochem. Soc.,1992,139:170
[8] Poursaee A,Hansson C M.Reinforcing steel passivation in mortar and pore solution[J].Cem. Concr. Res.,2007,37:1127
[9] Liu M,Cheng X Q,Li X G,et al.Corrosion behavior of Cr modified HRB400 steel rebar in simulated concrete pore solution[J].Constr. Build. Mater.,2015,93:884
[10] Liu R,Jiang L H,Xu J X,et al.Influence of carbonation on chloride-induced reinforcement corrosion in simulated concrete pore solutions[J].Constr. Build. Mater.,2014,56:16
[11] Williamson J,Isgor O B.The effect of simulated concrete pore solution composition and chlorides on the electronic properties of passive films on carbon steel rebar[J].Corros. Sci.,2016,106:82
[12] Liu M,Cheng X Q,Li X G,et al.Corrosion behavior of low-Cr steel rebars in alkaline solutions with different pH in the presence of chlorides[J]. J. Electroanal. Chem.,2017,803:40
[13] Zhou C,Tan H L,Liu M,et al.Electrochemical corrosion behavior of Cr modified steel rebars in cement extract solution[J]. J. Build. Mater.,2016,19:647
[13] (周成,谭何灵,刘明等.含Cr钢筋在水泥萃取液中的电化学腐蚀行为[J].建筑材料学报,2016,19:647
[14] Luo H,Su H Z,Dong C F,et al.Electrochemical and passivation behavior investigation of ferritic stainless steel in alkaline environment[J].Constr. Build. Mater.,2015,96:502
[15] Freire L,Catarino M A,Godinho M I,et al.Electrochemical and analytical investigation of passive films formed on stainless steels in alkaline media[J].Cem. Concr. Comp.,2012,34:1075
[16] Faichuk M G,Ramamurthy S,Lau W M.Electrochemical behaviour of Alloy 600 tubing in thiosulphate solution[J].Corros. Sci.,2011,53:1383
[17] Volpi E,Olietti A,Stefanoni M,et al.Electrochemical characterization of mild steel in alkaline solutions simulating concrete environment[J]. J. Electroanal. Chem.,2015,736:38
[1] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3] 张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[4] 严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[5] 丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[6] 刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[7] 廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na2CO3+NaHCO3溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[8] 李广宇, 雷明凯. γΝ相在硼酸溶液中钝化膜的组成及其半导体特性研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 47-53.
[9] 严寒, 赵晴, 杜楠, 胡彦卿, 王力强, 王帅星. 镀锌层三价铬钝化成膜过程及耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 547-553.
[10] 王彦亮,陈旭,王际东,宋博,范东升,何川. 316L不锈钢在不同pH值硼酸溶液中的电化学行为研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[11] 张天翼,吴俊升,郭海龙,李晓刚. 模拟海水中HSO3-对2205双相不锈钢钝化膜成分及耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 535-542.
[12] 张建春,蒋金洋,李阳,施锦杰,左龙飞,王丹芊,麻晗. 耐海水腐蚀钢筋00Cr10MoV在模拟混凝土孔隙液中钝化膜的研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 441-449.
[13] 王胜刚, 孙淼, 龙康. 紫外光电子能谱和X射线光电子能谱表征在金属材料腐蚀中的应用[J]. 中国腐蚀与防护学报, 2016, 36(4): 287-294.
[14] 冯林,王燕华,钟莲,王佳,李爱娇,金晓晓. 短期贮存对金属铜腐蚀电化学行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 375-380.
[15] 吴欣强,付尧,柯伟,徐松,冯兵,胡波涛,陆佳政. 高氮奥氏体不锈钢的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(3): 197-204.