中国腐蚀与防护学报  2015, Vol. 35 Issue (2): 169-176    DOI: 10.11902/1005.4537.2014.039
  论文 本期目录 | 过刊浏览 |
金属罐内涂层破损区气相定位检测局部电化学探头技术的研究
王雪莹1, 王佳1, 2, 刘在健1, 丁健1, 王海杰1
1. 中国海洋大学化学化工学院 青岛 266100; 2. 中国科学院金属研究所 金属腐蚀与防护国家重点实验室 沈阳 110016
Local Electrochemical Probe for Detecting Coating Defects on Inner Wall of Metal Can in Atmosphere
WANG Xueying1, WANG Jia1, 2, LIU Zaijian1, DING Jian1, WANG Haijie1
1. College of Chemistry and Chemical Engineering, Ocean University of China, Qingdao 266100, China; 2. State Key Laboratory for Corrosion and Protection, Shenyang 110016, China
全文: PDF(1975 KB)   HTML
摘要: 开发了能够在四维圆柱空间内定位检测罐内涂层破损区的气相局部电化学检测探头装置,可实现在气相环境中扫描测量罐内圆柱区和罐底平面区涂层表面的电化学状态,准确定位和评价涂层破损区。本文采用该装置定位检测了金属罐底缩区、焊缝区、底面区和罐体区的开路电位及电化学阻抗响应,并根据其相应的变化判断涂层破损区位置和程度。结果表明,该装置能够在气相环境中准确定位检测金属罐内平面和柱面区域的涂层位置和破损状态,在实验室具有较高的实用价值。
关键词 气相局部电化学探头金属罐涂层破损开路电位电化学阻抗谱    
Abstract:A local electrochemical probe was designed and set up as a means for detecting coating defects on inner wall of metal can in atmosphere. This device could detect and position coating defects on inner wall in four-dimensional manner. The probe could scan the planar and cylindrical areas of the inner wall of metal can in atmosphere to reveal a map of electrochemical signals of the scanned area, thereby coating defects could be evaluated and positioned accurately. As an example, OCP and EIS of the bottom shrinkage area, weld area, bottom area and sidewalls of a metal can were detected respectively. The result showed that this device could accurately position and evaluate the status of coating defects on planar and cylindrical area for the inner wall of a metal can in atmosphere. In summary, the local electrochemical probe had high practical value in laboratory.
Key wordslocal electrochemical probe    metal can    coating defect    open circuit potential    electrochemical impedance spectroscopy
收稿日期: 2014-04-01     
ZTFLH:  O646.6  
通讯作者: 通讯作者:王佳,E-mail:jwang@ouc.edu.cn,研究方向为腐蚀电化学     E-mail: jwang@ouc.edu.cn
作者简介: 王雪莹,女,1989年生,硕士生

引用本文:

王雪莹, 王佳, 刘在健, 丁健, 王海杰. 金属罐内涂层破损区气相定位检测局部电化学探头技术的研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 169-176.
WANG Xueying, WANG Jia, LIU Zaijian, DING Jian, WANG Haijie. Local Electrochemical Probe for Detecting Coating Defects on Inner Wall of Metal Can in Atmosphere. Journal of Chinese Society for Corrosion and protection, 2015, 35(2): 169-176.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2014.039      或      https://www.jcscp.org/CN/Y2015/V35/I2/169

img8801  局部电化学检测探头装置构造图
img8831  XYZθ
grp8870  轴四维扫描移动装置构造图
grp88B0  样品罐1和2在5%NaCl溶液体系中的EIS
grp898B  底缩区涂层开路电位随时间和位置的变化图
img89EA  底缩区涂层Bode模值图和阻抗模值随位置变化图
grp8A39  底缩区涂层破损处腐蚀形貌图
grp8A59  焊缝区涂层稳定开路电位随位置变化图
img8A79  焊缝区涂层阻抗模值随位置变化图
grp8AB9  焊缝区涂层破损处腐蚀形貌图
grp8AF8  罐底区涂层稳定开路电位随位置变化图
img8B28  底面区涂层阻抗模值随位置变化图
grp8B67  罐底区涂层缺陷处腐蚀形貌图
img8B97  罐壁区涂层稳定开路电位和阻抗模值随位置变化
grp8BC7  罐壁区涂层缺陷处腐蚀形貌图
grp8C25  不同尺寸涂层缺陷的阻抗谱响应图
[1] Guo H B, Zeng Q Z, Wang Y Q. Safety of the food packaging mate-rials and its strategies [J]. Mod. Food Sci. Technol., 2006, 22(3): 193 (郭恒斌, 曾庆祝, 王雅卿. 食品包装材料的安全性及其对策 [J]. 现代食品科技, 2006, 22 (3): 193)
[2] Zhang W, Wang J, Zhao Z Y, et al. Studies on deterioration process of organic coatings using EIS and SKP [J]. Chem. J. Chin. Univ., 2009, 30(4): 762 (张伟, 王佳, 赵增元等. 有机涂层失效过程的电化学阻抗和电位分布响应特征 [J]. 高等学校化学学报, 2009, 30(4): 762)
[3] Luo H, Xiao K, Dong C F, et al. Development of microzone electrochemical studies of metallic corrosion II: Local electrochemical impedance spectroscopy [J]. Corros. Prot., 2009, 30(8): 511 (骆鸿, 肖葵, 董超芳等. 金属腐蚀微区电化学研究进展II: 局部电化学阻抗谱 [J]. 腐蚀与防护, 2009, 30(8): 511)
[4] Zhong C, Tang X, Cheng Y F. Corrosion of steel under the defect coating studied by localized electrochemical impedance spectroscopy [J]. Electrochim. Acta, 2008, 53(14): 4740
[5] Pernkopf W, Sagl M, Fafilek G, et al. Applications of microelectrodes in impedance spectroscopy [J]. Solid State Ionics, 2005, 176 (25-28): 2031
[6] Gao Z M, Wang X, Zhang X L. On site detection of grounded grids corrosion with electrochemical methods [A]. Seventh Conference of Mainland-Taiwan Meterial Corrosion and Protection [C]. Kunming, 2010 (高志明, 王鑫, 张秀丽. 接地网腐蚀现场电化学检测 [A]. 第七届海峡两岸材料腐蚀与防护研讨会论文集 [C]. 昆明, 2010)
[7] Li W. EIS studies on gegradation of epoxy heavy-duty corrosion protection coating systems [D]. Beijing: Beijing University of Che-mical Technology, 2007 (李玮. 环氧重防腐涂层体系失效过程的电化学阻抗谱研究 [D]. 北京: 北京化工大学, 2007)
[8] Zhao Y H, Jiang C, Song L H, et al. Corrosion behavior of metal cans for drinks [J]. Corros. Sci. Prot. Technol., 2012, 24(3): 223 (赵宇晖, 江超, 宋莉华等. 金属饮料罐腐蚀行为及其作用机理研究 [J]. 腐蚀科学与防护技术, 2012, 24(3): 223)
[9] Scantleburya J D, Galic′b K. The application of AC impedance to study the performance of lacquered aluminium specimens in acetic acid solution [J]. Prog. Org. Coat., 1997, 31(3): 201
[10] Tian H, Wang Q L, Tao S Y, et al. Open circuit potential method in microbial fuel cell study [J]. J. Shenyang Normal Univ. (Nat. Sci.), 2012, 30(3): 386
(田红, 王清林, 陶思源等. 光合细菌燃料电池的开路电位法研究[J]. 沈阳师范大学学报 (自然科学版), 2012, 30(3): 386)
[11] Zhang W, Wang J, Zhao Z Y. Analysis of deterioration process of organic coatings using multi-parameter correlation analysis method [J]. Corros. Sci. Prot. Technol., 2010, 22(4): 319 (张伟, 王佳, 赵增元. 腐蚀电化学多参数相关法研究有机涂层失效子过程特征 [J]. 腐蚀科学与防护技术, 2010, 22(4): 319)
[1] 曹京宜, 杨延格, 方志刚, 寿海明, 李亮, 冯亚菲, 王兴奇, 褚广哲, 赵伊. 淡水舱涂层在不同水环境中的失效行为研究[J]. 中国腐蚀与防护学报, 2021, 41(2): 209-218.
[2] 曹京宜, 方志刚, 李亮, 冯亚菲, 王兴奇, 寿海明, 杨延格, 褚广哲, 殷文昌. 国产镀锌钢在不同水环境中的腐蚀行为:I淡水和盐水[J]. 中国腐蚀与防护学报, 2021, 41(2): 169-177.
[3] 曹京宜, 方志刚, 冯亚菲, 李亮, 杨延格, 寿海明, 王兴奇, 臧勃林. 国产镀锌钢在不同水环境中的腐蚀行为:II反渗透水和调质水[J]. 中国腐蚀与防护学报, 2021, 41(2): 178-186.
[4] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[5] 王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[6] 达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[7] 达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[8] 邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[9] 邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[10] 曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II:涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[11] 张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[12] 梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[13] 孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[14] 王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO3溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[15] 王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.